Polyolefin, Enhanced TPO POLYTROPE® STR 1042EU-01 NATURAL A SCHULMAN USA
0
مقایسهبرگه داده فنی
| شرایط آزمون | روش آزمون | نتیجه آزمون | |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 860 J/m |
| Flexural modulus | 23°C | ISO 178 | 2510 MPa |
| Charpy Notched Impact Strength | -30°C | ISO 179 | 4.1 kJ/m² |
| 23°C | ISO 179 | 62 kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 53 J/m |
| gloss | 60°,3180µm,热塑,光滑 | ISO 2813 | 20to40 |
| melt mass-flow rate | 230°C/2.16kg | ISO 1133 | 0.50 g/10min |
| Shrinkage rate | 23°C,24小时,3.18mm | ISO 294-4 | 0.70to0.90 % |
| tensile strength | Yield | ASTM D638 | 22.9 MPa |
| 屈服,23°C3 | ISO 527-2 | 23.6 MPa | |
| Tensile strain | 断裂,233°C | ISO 527-2 | >200 % |
| Impact strength of cantilever beam gap | -30°C | ISO 180 | 4.7 kJ/m² |
| 23°C | ISO 180 | 54 kJ/m² | |
| Dart impact | -30°C,TotalEnergy,韧性破坏 | ASTM D3763 | 48.6 J |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/Bf | 114 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 60.2 °C | |
| Linear coefficient of thermal expansion | MD:-30到100°C | ASTME831 | 4.5E-05 cm/cm/°C |
| TD | ASTME831 | 1.3E-04 cm/cm/°C | |
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| density | ISO 1183 | 1.16 g/cm³ |