| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | 23°C | ISO 1183 | 1.37 g/cm³ |
| Shrinkage rate | 横向流量 : 3.00 mm | 内部方法 | 0.60 - 0.90 % |
| Shrinkage rate | 流量 : 3.00 mm | 内部方法 | 0.20 - 0.50 % |
| Water absorption rate | 24 hr, 23°C | ISO 62 | 0.60 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 5.5 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | M 计秤, 23°C | ISO 2039-2 | 97 |
| Rockwell hardness | R 计秤, 80°C | ISO 2039-2 | 24 |
| Rockwell hardness | R 计秤, 23°C | ISO 2039-2 | 121 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 0.79 mm | UL 94 | HB |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | -40°C | ISO 527-2 | 235 Mpa |
| tensile strength | 23°C | ISO 527-2 | 190 Mpa |
| tensile strength | 80°C | ISO 527-2 | 120 Mpa |
| Tensile strain | 断裂, -40°C | ISO 527-2 | 2.0 % |
| Tensile strain | 断裂, 23°C | ISO 527-2 | 2.5 % |
| Tensile strain | 断裂, 80°C | ISO 527-2 | 5.0 % |
| Flexural modulus | -40°C | ISO 178 | 11600 Mpa |
| Flexural modulus | 23°C | ISO 178 | 9500 Mpa |
| Flexural modulus | 80°C | ISO 178 | 5800 Mpa |
| bending strength | -40°C | ISO 178 | 325 Mpa |
| bending strength | 23°C | ISO 178 | 290 Mpa |
| bending strength | 80°C | ISO 178 | 190 Mpa |
| compression stress | -40°C | ISO 604 | 250 Mpa |
| compression stress | 23°C | ISO 604 | 180 Mpa |
| compression stress | 80°C | ISO 604 | 110 Mpa |
| shear strength | 23°C | ASTM D732 | 95.0 Mpa |
| Taber abraser | 1000 Cycles | ISO 9352 | 0.400 mg |
| Friction coefficient - vs. Metal | | Suzuki Method | 0.15 |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | -40°C | ISO 179 | 10 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179 | 13 kJ/m² |
| Impact strength of simply supported beam without notch | -40°C | ISO 179 | 60 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 65 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Volume resistivity | | IEC 60093 | 1.0E+13 ohms·cm |
| dielectric strength | | IEC 60243-1 | 20 KV/mm |
| dielectric constant | 23°C, 50 Hz | IEC 60250 | 4.60 |
| dielectric constant | 23°C, 1 kHz | IEC 60250 | 4.40 |
| dielectric constant | 23°C, 1 MHz | IEC 60250 | 3.90 |
| Dissipation Factor | 23°C, 50 Hz | IEC 60250 | 0.020 |
| Dissipation Factor | 23°C, 1 kHz | IEC 60250 | 0.020 |
| Dissipation Factor | 23°C, 1 MHz | IEC 60250 | 0.020 |
| arc resistance | | UL 746 | 114 sec |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 262 °C |
| melting temperature | | DSC | 265 °C |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 2.0E-5 - 3.0E-5 cm/cm/°C |
| specific heat | | | 1800 J/kg/°C |
| thermal conductivity | | | 0.40 W/m/K |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.