| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | 23°C | ISO 1183 | 1.18 g/cm³ |
| melt mass-flow rate | 330℃，2.16kg330℃/2.16 kg | ISO 1133 | 46 g/10min |
| Melt volume flow rate | 330℃，2.16 kg330℃/2.16 kg | ISO 1133 | 45 cm3/10min |
| Shrinkage rate | TD：2.0 mmAcross Flow : 0.0787 in | ISO 294-4 | 0.75 % |
| Shrinkage rate | MD：2.0 mmFlow : 0,0787 in | ISO 294-4 | 0.75 % |
| Water absorption rate | 饱和，23℃饱和，23℃ | ISO 62 | 0.3 % |
| Water absorption rate | 平衡，23℃，50% RH平衡，23℃，50% RH | ISO 62 | 0.12 % |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| refractive index | | ISO 489 | 1.578 |
| transmittance | 1000 µm1000 µm | ISO 13468-2 | 89 % |
| Supplementary Information | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| electrolytic corrosion | 23℃23℃ | IEC 60426 | A1 |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of simply supported beam without notch | -30℃-30°C | ISO 179/1eU | No Break |
| Impact strength of simply supported beam without notch | 23℃23°C | ISO 179/1eU | No Break |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | 23℃23℃ | ISO 527-1-2 | 2400 Mpa |
| tensile strength | 屈服，23℃屈服，23℃ | ISO 527-2/50 | 68 Mpa |
| Tensile strain | 屈服，23℃屈服，23℃ | ISO 527-2/50 | 6.2 % |
| Nominal tensile fracture strain | 23℃23℃ | ISO 527-2/50 | > 50 % |
| Flexural modulus | 23℃23℃3 | ISO 178 | 2400 Mpa |
| bending strength | 23℃ | ISO 178 | 100 Mpa |
| ball-indentation hardness | | ISO 2039-1 | 120 Mpa |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | IEC 60093 | 10000000000000000 ohms |
| Volume resistivity | 23℃23℃ | IEC 60093 | 100000000000000000 ohms·cm |
| dielectric strength | 23 ℃，1 mm23℃，1.00 mm | IEC 60243-1 | 35 KV/mm |
| relative permittivity | 23℃，100 Hz23°C, 100 Hz | IEC 60250 | 3 |
| relative permittivity | 23℃，1 MHz23°C, 1 MHz | IEC 60250 | 2.9 |
| Dissipation Factor | 23℃，100 Hz23°C, 100 Hz | IEC 60250 | 0.001 |
| Dissipation Factor | 23℃，1 MHz23°C, 1 MHz | IEC 60250 | 0.009 |
| Compared to the Leakage Tracking Index (CTI) | 解决方案 ASolution A | IEC 60112 | PLC 2 |
| Compared to the Leakage Tracking Index (CTI) | 解决方案 BSolution B | IEC 60112 | PLC 4 |
| UL flame retardant rating | 1.50 mm | UL 94 | HB |
| UL flame retardant rating | 3.00 mm | UL 94 | HB |
| Glow wire combustion index (GWFI) | 2.0 mm2.0 mm | IEC 60695-2-12 | 900 °C |
| Limiting Oxygen Index | | ISO 4589-2 | 26 % |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8 MPa，未退火1.8 MPa，未退火，HDT | ISO 75-2/A | 138 °C |
| vicat | B120B120 | ISO 306/B120 | 158 °C |
| Linear coefficient of thermal expansion | TD：23~55℃TD：23 到 55℃ | ISO 11359-2 | 0.000065 1/℃ |
| Linear coefficient of thermal expansion | MD：23~55℃MD：23 到 55℃ | ISO 11359-2 | 0.000065 1/℃ |
| Relative Heat Index (RTI) | 电气性能电气性能 | UL 746 | 140 °C |
| Relative Heat Index (RTI) | 强度机械性能强度机械性能 | UL 746 | 140 °C |
| Relative Heat Index (RTI) | 冲击机械性能冲击机械性能 | UL 746 | 130 °C |