EPE 5110G DOW USA

مقایسه

برگه داده فنی

optical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
turbidity	50.8μm	ASTM D1003	13 %
gloss	45°,50.8μm	ASTM D2457	60

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Vicat softening temperature		ASTM D1525	111 °C
Melting temperature		Internal Method	123 °C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
melt mass-flow rate	190°C/2.16kg	ASTM D1238	0.85 g/10min
density		ASTM D792	0.926 g/cm³

film	شرایط آزمون	روش آزمون	نتیجه آزمون
Secant modulus	2%Secant,TD:51μm	ASTM D882	330 MPa
Secant modulus	Secant modulus	2%Secant,MD:51μm	ASTM D882	277 MPa
Thin film puncture strength	51μm	Internal Method	97.0 N
Thin film puncture strength	Thin film puncture strength	51μm	Internal Method	6.91 J
film thickness			51 µm
Initial sealing temperature	51μm	Internal Method	120 °C
Elmendorf tear strength	TD:51μm	ASTM D1922	1100 g
Elmendorf tear strength	Elmendorf tear strength	MD:51μm	ASTM D1922	560 g
Dart impact	51μm	ASTM D1709B	410 g
elongation	TD:Break,51μm	ASTM D882	660 %
elongation	elongation	MD:Break,51μm	ASTM D882	600 %
tensile strength	TD:Break,51μm	ASTM D882	51.9 MPa
	tensile strength	MD:Break,51μm	ASTM D882	57.5 MPa
		tensile strength	TD:Yield,51μm	ASTM D882	14.6 MPa
		tensile strength	tensile strength	MD:Yield,51μm	ASTM D882	13.9 MPa