LDPE 2001 STYRON US
39
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 0.40 g/10min |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| gloss | 45°,50.8µm | ASTM D2457 | 91 |
| Haze ratio | 50.8µm | ASTM D1003 | 4.8 % |
| film | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| film strength | TD:51µm | ASTM D882 | 94.9 J/cm³ |
| Secant modulus | 1%正割,MD:51µm | ASTM D882 | 250 Mpa |
| 1%正割,TD:51µm | ASTM D882 | 272 Mpa | |
| tensile strength | MD:屈服,51µm | ASTM D882 | 15.4 Mpa |
| TD:屈服,51µm | ASTM D882 | 14.2 Mpa | |
| MD:断裂,51µm | ASTM D882 | 30.2 Mpa | |
| TD:断裂,51µm | ASTM D882 | 25.4 Mpa | |
| elongation | MD:断裂,51µm | ASTM D882 | 440 % |
| TD:断裂,51µm | ASTM D882 | 600 % | |
| Dart impact | 51µm | ASTM D1709A | 120 g |
| film thickness | 51 µm | ||
| Thin film puncture strength | 51µm | 内部方法 | 5.46 J/cm³ |
| film strength | MD:51µm | ASTM D882 | 94.5 J/cm³ |
| Elmendorf tear strength | MD:51µm | ASTM D1922 | 280 g |
| TD:51µm | ASTM D1922 | 570 g |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| melting temperature | 内部方法 | 113 °C |