| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | g/cm³ | 1.29 -- |
| Water absorption rate | 饱和,23°C | % | 5.5 -- |
| Water absorption rate | 平衡,23°C,50%RH | % | 1.7 -- |
| Water absorption rate | after24himmersioninwater:23°C | mg | 30.0 -- |
| Water absorption rate | after96himmersioninwater:23°C | mg | 56.0 -- |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| ball-indentation hardness | | MPa | 165 -- |
| Rockwell hardness | M计秤 | | 76 -- |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 3.00mm | | HB -- |
| UL flame retardant rating | 6.00mm | | HB -- |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile creep modulus | 1000hr | MPa | 26.0 18.0 |
| compression stress | 5%应变 | MPa | 90.0 -- |
| compression stress | 2%应变 | MPa | 55.0 -- |
| compression stress | 1%应变 | MPa | 28.0 -- |
| Tensile modulus | 23°C | MPa | 5900 3200 |
| tensile strength | 屈服,23°C | MPa | 100 75.0 |
| Tensile strain | 断裂,23°C | % | 5.0 12 |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | | kJ/m² | 6.0 -- |
| Impact strength of simply supported beam without notch | | kJ/m² | >50 -- |
| Impact strength of cantilever beam gap | | kJ/m² | 6.0 11 |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Volume resistivity | | ohms·cm | >1.0E+14 >1.0E+13 |
| dielectric strength | | kV/mm | 30 20 |
| relative permittivity | 100Hz | | 3.90 6.90 |
| relative permittivity | 1MHz | | 3.60 3.90 |
| Dissipation Factor | 100Hz | | 0.012 0.19 |
| Dissipation Factor | 1MHz | | 0.014 0.040 |
| Surface Resistivity | | ohms | >1.0E+13 >1.0E+12 |
| Compared to the Leakage Tracking Index (CTI) | | V | PLC 1 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | °C | 150 -- |
| melting temperature | | °C | 255 -- |
| Linear coefficient of thermal expansion | MD：23到60°C | cm/cm/°C | 5E-05 -- |
| Linear coefficient of thermal expansion | MD：23到100°C | cm/cm/°C | 6E-05 -- |
| thermal conductivity | | W/m/K | 0.30 -- |
| Minimum operating temperature | | °C | -20 -- |
| maximum service temperature | inaircontinuosly | °C | 120 -- |
| maximum service temperature | inairforshortperiods | °C | 240 -- |