برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Shrinkage rate | | ASTM D-955 | 0.4-0.6 % |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| transmittance | | ASTM D-1003 | 88 % |
| Basic performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| melt mass-flow rate | 220℃,10kg | ISO 1133 | 29 g/10min |
| Water absorption rate | | ISO 62 | 0.3 % |
| density | | ISO 1183 | 1.07 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | | ISO 527 | 45 Mpa |
| bending strength | | ISO 178 | 65 Mpa |
| Flexural modulus | | ISO 178 | 1900 Mpa |
| Charpy Notched Impact Strength | 23℃ | ISO 179/1eA | 15 KJ/m |
| Charpy Notched Impact Strength | -30℃ | ISO 179/1eA | 7 KJ/m |
| Impact strength of cantilever beam gap | 23℃,6.4mm | ASTM D-256 | 150 J/m |
| Impact strength of cantilever beam gap | -30℃,6.4mm | ASTM D-256 | 70 J/m |
| Rockwell hardness | | ISO 2039 | R108 |
| Other performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| JHOPA | | | 抗PL |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.80MPa,12.7mm，HDT | ISO 75/A | 76 °C |
| Heat distortion temperature | 1.82MPa,12.7mm，HDT | ASTM D-648 | 86 °C |
| Ball indentation temperature | | | 90 °C |
| combustibility | | UL 94 | HB |