impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Suspended wall beam without notch impact strength	23°C	ASTM D4812	3200	J/m
Dart impact	23°C7	ASTM D3029	43.4	J
Dart impact	Dart impact	23°C	ASTM D3029	43.4	J
flammability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
UL flame retardant rating	0.46mm	UL 94	HB
	UL flame retardant rating	0.64mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	5VA
Extreme Oxygen Index		ASTM D2863	30	%
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
tensile strength	Yield	ASTM D638	48.3	Mpa
tensile strength	tensile strength	Break	ASTM D638	48.3	Mpa
elongation	Break	ASTM D638	110	%
Bending modulus	50.0mmSpan	ASTM D790	2070	Mpa
bending strength	Yield,50.0mmSpan	ASTM D790	82.7	Mpa
bending strength	bending strength	Break,50.0mmSpan	ASTM D790	82.7	Mpa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	138	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	98.9	°C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	9.2E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：60to138°C	ASTME831	1.2E-04	cm/cm/°C
RTI Elec		UL 746	120	°C
RTI Imp		UL 746	120	°C
RTI		UL 746	140	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Specific volume		ASTM D792	0.750	cm³/g
Melt Volume Flow Rate (MVR)	250°C/5.0kg	ISO 1133	8.00	cm3/10min
Shrinkage rate	MD3	Internal Method	1.0-1.4	%
	Shrinkage rate	MD4	Internal Method	0.80-1.1	%
		Shrinkage rate	TD3	Internal Method	1.2-1.6	%
		Shrinkage rate	Shrinkage rate	TD4	Internal Method	0.90-1.3	%
Water absorption rate	24hr	ASTM D570	0.080	%
Outdoor applicability		UL 746C	f2
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Volume resistivity		ASTM D257	>1.2E+16	ohms·cm
Dielectric strength	1.60mm,inOil	ASTM D149	25	KV/mm
	Dielectric strength	3.20mm,inAir	ASTM D149	19	KV/mm
	Dielectric strength	Dielectric strength	3.20mm,inOil	ASTM D149	19	KV/mm
Dielectric constant	100Hz	ASTM D150	3.20
Dielectric constant	Dielectric constant	1MHz	ASTM D150	3.20
Dissipation factor	100Hz	ASTM D150	3E-03
Dissipation factor	Dissipation factor	1MHz	ASTM D150	0.030
Arc resistance		ASTM D495	PLC6
Compared to the anti leakage trace index	CTI	UL 746	PLC 2
High arc combustion index	HAI	UL 746	PLC 3
High voltage arc tracing rate	HVTR	UL 746	PLC 3
Hot wire ignition	HWI	UL 746	PLC 2
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Rockwell hardness	R-Scale	ASTM D785	117

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.