PPS SUSTEEL® P-01 TOSOH JAPAN
57
مقایسه
مشاهده قیمتهابرگه داده فنی
| processability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Shrinkage rate | 机械方向 | ASTM D-955 | 0.3 % |
| 横向 | ASTM D-955 | 0.7 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| elongation | ASTM D-638 | 1.4 % | |
| tensile strength | ASTM D-638 | 152(1550) MPa(KG/cm | |
| Rockwell hardness | ASTM D-785 | 123 Rscal | |
| bending strength | ASTM D-790 | 250(2550) MPa(KG/cm | |
| Tensile modulus | ASTM D-790 | 17(1.7) | |
| Impact strength of cantilever beam gap | 缺口 | ASTM D-955 | 59(6) J/m(kg.cm/cm) |
| 无缺口 | ASTM D-955 | 343(35) J/m(kg.cm/cm) |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Volume resistivity | ASTM D-257 | 1×10 Ω.cm | |
| dielectric constant | 1MHz | ASTM D-150 | 4.7 |
| Dissipation Factor | 1MHz | ASTM D-150 | 0.0015 |
| dielectric strength | ASTM D-149 | 14 KV/mm |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Linear coefficient of thermal expansion | Tosoh Method | 2.0 | |
| Heat distortion temperature | 18.6kg/cm，HDT | ASTM D-648 | ＞260 °C |
| Linear coefficient of thermal expansion | 0.37(0.32) W/M.K(kcal/m.hr.℃) |