AES HW600G
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB CLASS | |
| gloss | 60° | ASTM D-523 | 88 |
| processability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Shrinkage rate | ASTM D-955 | 0.4～0.7 % |
| Basic performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| melt mass-flow rate | 220℃×10kg | ASTM D-1238 | 20 g/10min |
| 200℃×5kg | ASTM D-1238 | 2.2 g/10min | |
| density | 23℃ | ASTM D-792 | 1.04 g/cm3 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23℃，3.2mm | ASTM D-256 | 13.0 kg.cm/cm |
| 23℃，6.4mm | ASTM D-256 | 15.0 kg.cm/cm | |
| elongation | 50mm/min | ASTM D-638 | 22 % |
| tensile strength | 50mm/min | ASTM D-638 | 550 Kg/cm2 |
| Rockwell hardness | R scale | ASTM D-785 | 105 R |
| Flexural modulus | 3mm/min | ASTM D-790 | 23000 Kg/cm2 |
| bending strength | 3mm/min | ASTM D-790 | 660 Kg/cm2 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Heat distortion temperature | 1/4″(18.6kg/ cm2)，HDT | ASTM D-648 | 90(194) ℃(℉) |