physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
density | | ASTM D792 | 1.20 g/cm³ |
density | 23°C | ISO 1183 | 1.19 g/cm³ |
Shrinkage rate | MD:3.20mm | ASTM D955 | 0.20to0.60 % |
hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Rockwell hardness | R计秤,23°C | ASTM D785 | 105 |
optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
transmissivity | 总计 | ASTM D1003 | 91.0 % |
transmissivity | Regular | ASTM D1003 | 89.0 % |
Haze ratio | | ASTM D1003 | 0.30 % |
flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
UL flame retardant rating | 3.0mm | UL 94 | V-2 |
Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Tensile strain | 屈服,23°C | ISO 527-2 | 4.0 % |
elongation | 断裂,23°C | ASTM D638 | 310 % |
Tensile strain | 断裂,23°C | ISO 527-2 | 210 % |
tensile strength | 屈服,23°C | ISO 527-2 | 47.0 MPa |
tensile strength | 断裂,23°C | ASTM D638 | 53.0 MPa |
tensile strength | 断裂,23°C | ISO 527-2 | 49.0 MPa |
elongation | 屈服,23°C | ASTM D638 | 5.0 % |
tensile strength | 屈服,23°C | ASTM D638 | 46.0 MPa |
Flexural modulus | 23°C | ASTM D790 | 1900 MPa |
Flexural modulus | 23°C | ISO 178 | 1750 MPa |
bending strength | 23°C | ISO 178 | 64.0 MPa |
bending strength | 屈服,23°C | ASTM D790 | 67.0 MPa |
Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Dart impact | -40°C,EnergyatPeakLoad | ASTM D3763 | 48.0 J |
Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 45.0 J |
Impact strength of cantilever beam gap | -40°C | ASTM D256 | 60 J/m |
Impact strength of cantilever beam gap | 23°C | ASTM D256 | 370 J/m |
Impact strength of cantilever beam gap | -40°C | ISO 180 | 6.3 kJ/m² |
Impact strength of cantilever beam gap | 23°C | ISO 180 | 30 kJ/m² |
Impact strength of cantilever beam gap | -40°C | ASTM D4812 | NoBreak |
Impact strength of cantilever beam gap | 23°C | ASTM D4812 | NoBreak |
Multi axis Instrumented Impact Energy | -40°C,能量到力量峰值 | ISO 6603-2 | 55.0 J |
Multi axis Instrumented Impact Energy | 23°C,能量到力量峰值 | ISO 6603-2 | 71.0 J |
Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Volume resistivity | 23°C | ASTM D257 | 1E+17 ohms·cm |
dielectric strength | 23°C | ASTM D149 | 17 kV/mm |
dielectric constant | 23°C,1kHz | ASTM D150 | 2.60 |
dielectric constant | 23°C,10kHz | ASTM D150 | 2.60 |
dielectric constant | 23°C,100kHz | ASTM D150 | 2.50 |
dielectric constant | 23°C,1MHz | ASTM D150 | 2.50 |
Dissipation Factor | 23°C,1kHz | ASTM D150 | 6E-03 |
arc resistance | | ASTM D495 | 123 sec |
Compared to the Leakage Tracking Index (CTI) | | ASTM D3638 | PLC 0 |
Dissipation Factor | 23°C,10kHz | ASTM D150 | 0.012 |
Dissipation Factor | 23°C,100kHz | ASTM D150 | 0.015 |
Dissipation Factor | 23°C,1MHz | ASTM D150 | 0.015 |
Surface Resistivity | | ASTM D257 | 1E+17 ohms |
Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Heat distortion temperature | 0.45MPa,未退火,HDT | ASTM D648 | 73.0 °C |
Heat distortion temperature | 0.45MPa,未退火,HDT | ISO 75-2/B | 73.0 °C |
Heat distortion temperature | 1.8MPa,未退火,HDT | ASTM D648 | 65.0 °C |
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/A | 66.0 °C |