HIPS STYRON A-TECH H9152T
37
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Shrinkage rate | ASTM D-955 | 0.40-0.70 % |
| Basic performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| melt mass-flow rate | 200℃/5kg | ASTM D-1238 | 5.0 g/10min |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| tensile strength | 屈服 | ASTM D-638 | 33.1 Mpa |
| 断裂 | ASTM D-638 | 30.3 Mpa | |
| elongation | 断裂 | ASTM D-638 | 40 % |
| Flexural modulus | ASTM D-790 | 2560 Mpa | |
| bending strength | ASTM D-790 | 58.6 Mpa | |
| Impact strength of cantilever beam gap | 23℃ | ASTM D-256 | 90.7 J/m |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa，退火，HDT | ASTM D-648 | 98.9 °C |
| vicat | ASTM D-1525 | 105 °C | |
| Linear coefficient of thermal expansion | Flow | ASTM D-696 | 0.000076 cm/cm/℃ |
| UL flame retardant rating | 1.50mm | UL 94 | HB |
| Heat distortion temperature | 1.80MPa，未退火，HDT | ASTM D-648 | 77.2 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.