| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | --2 | ASTM D792 | 1.61 g/cm³ |
| density | 23°C | ISO 1183 | 1.61 g/cm³ |
| melt mass-flow rate | 250°C/2.16kg | ASTMD1238 | 25 g/10min |
| Shrinkage rate | MD:23°C | ASTM D955 | 0.30to0.60 % |
| Shrinkage rate | 23°C | ISO 294-4 | 0.30to0.60 % |
| Water absorption rate | 平衡,23°C | ASTM D570 | 0.080 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.080 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.6mm | UL 94 | V-0 |
| UL flame retardant rating | 3.2mm | UL 94 | V-0 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| elongation | Break | ISO 527-2/5 | 2.0 % |
| tensile strength | --3 | ASTM D638 | 120 MPa |
| tensile strength | -- | ISO 527-2/5 | 120 MPa |
| elongation | 断裂3 | ASTM D638 | 1.9 % |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 9500 MPa |
| Flexural modulus | --4 | ISO 178 | 9800 MPa |
| bending strength | 50.0mm跨距 | ASTM D790 | 180 MPa |
| bending strength | --4 | ISO 178 | 186 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 75 J/m |
| Impact strength of cantilever beam gap | 23°C5 | ISO 180/1A | 7.0 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 3 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTMD648 | 200 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.