PC Lupoy® 1302HP-07

مقایسه

برگه داده فنی

physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ASTM D792	1.20 g/cm³
melt mass-flow rate	300°C/1.2kg	ASTM D1238	7.0 g/10min
Shrinkage rate	MD	ASTM D955	0.50to0.70 %
Water absorption rate	23°C,24hr	ASTM D570	0.15 %
Water absorption rate	Water absorption rate	平衡,23°C,50%RH	ASTM D570	0.32 %

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Rockwell hardness	M计秤	ASTM D785	74
Rockwell hardness	Rockwell hardness	R-Scale	ASTM D785	118

optical performance	روش آزمون	نتیجه آزمون
Haze ratio	ASTM D1003	0.70to1.5 %
refractive index	ASTM D542	1.586
transmissivity	ASTM D1003	89.0 %

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
Limiting Oxygen Index		ASTM D2863	26 %
Average degree of combustion		ASTM D635	3 cm
UL flame retardant rating	0.50mm	UL 94	V-2
	UL flame retardant rating	1.6mm	UL 94	V-2
		UL flame retardant rating	2.5mm	UL 94	V-2
		UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	V-2
GWIT	2.0mm	IEC 60695-2-13	850 °C

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus		ASTM D638	2410 MPa
tensile strength	Yield	ASTM D638	60.0 MPa
tensile strength	tensile strength	Break	ASTM D638	72.0 MPa
elongation	Yield	ASTM D638	6.0 %
elongation	elongation	Break	ASTM D638	150 %
Flexural modulus		ASTM D790	2410 MPa
bending strength		ASTM D790	96.0 MPa
wear resistance	雾度变化	ASTM D1004	45 %

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256	90 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D256	NoBreak
InstrumentedDartImpact	23°C,3.20mm,TotalEnergy	ASTM D3763	90.0 J

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Volume resistivity	23°C	ASTM D257	2E+17 ohms·cm
dielectric strength		ASTM D149	17 kV/mm
dielectric constant	60Hz	ASTM D150	3.00
Dissipation Factor	60Hz	ASTM D150	1E-03
Compared to the Leakage Tracking Index (CTI)	2.00mm	IEC 60112	PLC 2

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	0.45MPa,Annealed,4.00mm，HDT	ASTM D648	145 °C
	Heat distortion temperature	1.8MPa,Unannealed,4.00mm，HDT	ASTM D648	129 °C
	Heat distortion temperature	Heat distortion temperature	1.8MPa,Annealed,4.00mm，HDT	ASTM D648	142 °C
vicat		ASTM D15255	151 °C
Ball pressure temperature		IEC 60598-1	>125 °C
Linear coefficient of thermal expansion	MD：-40到82°C	ASTM D696	6.8E-05 cm/cm/°C