| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ISO 1183 | 1.37 g/cm³ |
| Melt volume flow rate | 360°C/10.0kg | ISO 1133 | 70.0 cm3/10min |
| Shrinkage rate | TD | ISO 294-4 | 0.86 % |
| Shrinkage rate | MD | ISO 294-4 | 0.82 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 2.2 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.80 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| ball-indentation hardness | | ISO 2039-1 | 154 Mpa |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 3.0mm | UL 94 | V-0 |
| UL flame retardant rating | 1.6mm | UL 94 | V-0 |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | 23°C | ISO 180 | 7.0 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180 | 7.5 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | NoBreak |
| Impact strength of simply supported beam without notch | -30°C | ISO 179 | NoBreak |
| Charpy Notched Impact Strength | 23°C | ISO 179 | 7.0 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO 179 | 7.5 kJ/m² |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | 23°C | ISO 527-2 | 2650 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2 | 85.0 Mpa |
| Tensile strain | 屈服,23°C | ISO 527-2 | 6.9 % |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 4 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.014 |
| Dissipation Factor | 100Hz | IEC 60250 | 1.7E-03 |
| dielectric constant | 1MHz | IEC 60250 | 3.80 |
| dielectric constant | 100Hz | IEC 60250 | 3.90 |
| dielectric strength | | IEC 60243-1 | 37 KV/mm |
| Volume resistivity | | IEC 60093 | >1.0E+13 ohms·cm |
| Surface Resistivity | | IEC 60093 | >1.0E+15 ohms |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| RTI Elec | 3.0mm | UL 746 | 180 °C |
| RTI Elec | 1.6mm | UL 746 | 180 °C |
| Linear coefficient of thermal expansion | MD | | 5.2E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 205 °C |
| RTI Str | 3.0mm | UL 746 | 190 °C |
| RTI Str | 1.6mm | UL 746 | 190 °C |
| RTI Imp | 3.0mm | UL 746 | 180 °C |
| RTI Imp | 1.6mm | UL 746 | 180 °C |