PCT LAVANTA® 5115 WH 224 SOLVAY USA

مقایسه مشاهده قیمت‌ها

برگه داده فنی

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
bending strength		ISO 178	108 Mpa
Bending modulus		ISO 178	6230 Mpa
Tensile strain	Break	ISO 527-2	1.5 %
tensile strength		ISO 527-2	73.3 Mpa
Tensile modulus		ISO 527-2	6730 Mpa

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Linear coefficient of thermal expansion	TD:200to250°C	ASTME831	1.4E-04 cm/cm/°C
	Linear coefficient of thermal expansion	TD:150to200°C	ASTME831	1.2E-04 cm/cm/°C
		Linear coefficient of thermal expansion	TD:100to150°C	ASTME831	1E-04 cm/cm/°C
			Linear coefficient of thermal expansion	TD:50to100°C	ASTME831	5.8E-05 cm/cm/°C
				Linear coefficient of thermal expansion	MD:200to250°C	ASTME831	2E-05 cm/cm/°C
					Linear coefficient of thermal expansion	MD:150to200°C	ASTME831	1.7E-05 cm/cm/°C
					Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD:50to100°C	ASTME831	2.9E-05 cm/cm/°C
Melting temperature		ISO 11357-3	289 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	214 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	269 °C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Shrinkage rate	MD	ASTM D955	0.39 %
Shrinkage rate	Shrinkage rate	TD	ASTM D955	1.2 %
Water absorption rate	24hr	ASTM D570	0.048 %

Supplementary Information	شرایط آزمون	روش آزمون	نتیجه آزمون
Light reflectance	620nm	ASTME1331	>96 %
	Light reflectance	540nm	ASTME1331	>95 %
	Light reflectance	Light reflectance	460nm	ASTME1331	>95 %

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.