PA12 Grilamid® L 25 H EMS-GRIVORY
0
مقایسهبرگه داده فنی
| شرایط آزمون | روش آزمون | نتیجه آزمون | |
|---|---|---|---|
| Continuous use temperature | --2 | °C | 100to120 -- |
| --3 | °C | 150 -- | |
| melting temperature | °C | 178 -- | |
| Charpy Notched Impact Strength | 23°C | kJ/m² | 8.0 10 |
| Impact strength of simply supported beam without notch | -30°C | 无断裂 | |
| 23°C | 无断裂 | ||
| Heat distortion temperature | 0.45MPa,未退火，HDT | °C | 115 -- |
| 1.8MPa,未退火，HDT | °C | 45.0 -- | |
| Linear coefficient of thermal expansion | MD | cm/cm/°C | 1.2E-04 -- |
| TD | cm/cm/°C | 1.4E-04 -- | |
| Surface Resistivity | ohms | -- 1E+12 | |
| Water absorption rate | 饱和,23°C | % | 1.5 -- |
| 平衡,23°C,50%RH | % | 0.70 -- | |
| Volume resistivity | ohms·cm | -- 1E+13 | |
| dielectric strength | kV/mm | 32 -- | |
| Compared to the Leakage Tracking Index (CTI) | V | -- | |
| tensile strength | Break | MPa | 50.0 50.0 |
| Tensile strain | Yield | % | 5.0 12 |
| Nominal tensile fracture strain | % | >50 >50 | |
| Charpy Notched Impact Strength | -30°C | kJ/m² | 6.0 7.0 |
| density | g/cm³ | 1.01 -- | |
| Shore hardness | 邵氏D,15秒 | 70 -- | |
| ball-indentation hardness | MPa | 70.0 -- | |
| Tensile modulus | MPa | 1600 1100 | |
| Flammability level | 0.8mm | HB -- | |
| tensile strength | Yield | MPa | 50.0 40.0 |