Copolyester Eastar™ DN001, Natural Eastman Chemical Company

توصیف محصول

گواهی‌نامه‌ها(0)

جدول خواص

توصیف محصول

گواهی‌نامه‌ها

No Data...

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Impact strength of cantilever beam gap	-40°C	ISO 180	7.4	kJ/m²
	Impact strength of cantilever beam gap	-40°C	ASTM D256	64	J/m
		Impact strength of cantilever beam gap	23°C	ASTM D256	NoBreak
			Impact strength of cantilever beam gap	23°C	ISO 180	130	kJ/m²
				Impact strength of cantilever beam gap	-40°C	ASTM D4218	NoBreak
				Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D4218	NoBreak
Multi axis Instrumented Impact Energy	-40°C,能量to力量峰值	ISO 6603-2	16.0	J
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy	23°C,能量to力量峰值	ISO 6603-2	14.0	J
flammability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
UL flame retardant rating	1.6mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	3.2mm	UL 94	HB
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
elongation	Yield,23°C	ASTM D638	5.0	%
Tensile strain	Yield,23°C,4.00mm	ISO 527-2	4.4	%
tensile strength	Yield,23°C,4.00mm	ISO 527-2	46.0	MPa
	tensile strength	Break,23°C	ASTM D638	52.0	MPa
	tensile strength	tensile strength	Break,23°C,4.00mm	ISO 527-2	47.0	MPa
elongation	Break,23°C	ASTM D638	330	%
Tensile strain	Break,23°C,4.00mm	ISO 527-2	230	%
Bending modulus	23°C	ASTM D790	1800	MPa
Bending modulus	Bending modulus	23°C,4.00mm	ISO 178	1800	MPa
bending strength	23°C,4.00mm	ISO 178	63.0	MPa
bending strength	bending strength	Yield,23°C	ASTM D790	66.0	MPa
Tensile modulus	23°C	ASTM D638	1800	MPa
tensile strength	Yield,23°C	ASTM D638	45.0	MPa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Vicat softening temperature	--	ISO 306/A	88.0	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B	79.0	°C
specific heat	60°C		1340	J/kg/°C
specific heat	specific heat	240°C		2050	J/kg/°C
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	74.0	°C
	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	74.0	°C
		Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	64.0	°C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	65.0	°C
Vicat softening temperature		ASTM D15252	88.0	°C
specific heat	导热系数(23°C)		0.19	W/m/K
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Water absorption rate	23°C,24hr	ISO 62	0.13	%
density		ASTM D792	1.23	g/cm³
density	density	23°C	ISO 1183	1.23	g/cm³
Shrinkage rate	MD：3.20mm	ASTM D955	0.20to0.50	%
Water absorption rate	23°C,24hr	ASTM D570	0.13	%
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Dissipation factor	23°C,10kHz	ASTM D150	0.012
	Dissipation factor	23°C,100kHz	ASTM D150	0.016
	Dissipation factor	Dissipation factor	23°C,1MHz	ASTM D150	0.018
Arc resistance		ASTM D495	66.0	sec
Dielectric constant	23°C,100kHz	ASTM D150	2.60
Dielectric constant	Dielectric constant	23°C,1MHz	ASTM D150	2.50
Dissipation factor	23°C,1kHz	ASTM D150	5.6E-03
Dielectric constant	23°C,1kHz	ASTM D150	2.70
Dielectric constant	Dielectric constant	23°C,10kHz	ASTM D150	2.70
Dielectric strength	23°C	ASTM D149	16	kV/mm
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Rockwell hardness	R-Sale,23°C	ASTM D785	105

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.