impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	15	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	75	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	10	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	70	kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	NoBreak
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	NoBreak
Dart impact	23°C,EnergyatPeakLoad	ASTM D3763	65.0	J
Dart impact	Dart impact	23°C,TotalEnergy	ASTM D3763	65.0	J
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Tensile modulus		ASTM D638	2310	Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	2300	Mpa
tensile strength	Yield	ASTM D638	62.1	Mpa
	tensile strength	Yield	ISO 527-2/50	60.0	Mpa
		tensile strength	Break	ASTM D638	68.9	Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	75.0	Mpa
elongation	Yield	ASTM D638	6.5	%
Tensile strain	Yield	ISO 527-2/50	6.0	%
elongation	Break	ASTM D638	140	%
Tensile strain	Break	ISO 527-2/50	140	%
Bending modulus	50.0mmSpan	ASTM D790	2340	Mpa
Bending modulus	Bending modulus		ISO 178	2250	Mpa
bending strength		ISO 178	95.0	Mpa
bending strength	bending strength	Yield,50.0mmSpan	ASTM D790	97.9	Mpa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	5.7E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	6E-05	cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	138	°C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	124	°C
		Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	132	°C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	124	°C
Vicat softening temperature		ASTM D152511	154	°C
	Vicat softening temperature	--	ISO 306/B50	143	°C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	140	°C
Ball Pressure Test	75°C	IEC 60695-10-2	Pass
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	6.2E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	6E-05	cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	135	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
melt mass-flow rate	300°C/1.2kg	ASTM D1238	7.0	g/10min
melt mass-flow rate	melt mass-flow rate	300°C/5.0kg	ASTM D1238	110	g/10min
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	6.50	cm3/10min
Shrinkage rate	MD：--2	Internal Method	0.50-0.70	%
	Shrinkage rate	MD：3.20mm	Internal Method	0.50-0.70	%
	Shrinkage rate	Shrinkage rate	TD：3.20mm	Internal Method	0.50-0.70	%
Water absorption rate	24hr	ASTM D570	0.15	%
	Water absorption rate	Saturation,23°C	ISO 62	0.35	%
	Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.15	%
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Rockwell hardness	R-Scale	ASTM D785	118