برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ISO 1183 | 1.90to2.00 g/cm³ |
| Apparent density | | ISO 60 | 0.70to1.00 g/cm³ |
| Shrinkage rate | MD | ISO 2577 | 0.30to0.50 % |
| Water absorption rate | 23°C,24hr | ISO 62 | <0.10 % |
| Shrinkage rate | | ISO 2577 | <0.050 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| Burning wire flammability index | | IEC 60695-2-12 | 900 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 900 °C |
| Supplementary Information | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Compression molding pressure | | | >5.00 MPa |
| Compression molding temperature | | | 150to190 °C |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 12to16 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 4.0to7.0 kJ/m² |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | | ISO 527-2 | 15000to18000 MPa |
| tensile strength | | ISO 527-2 | 60.0to80.0 MPa |
| Flexural modulus | | ISO 178 | 20000to23000 MPa |
| bending strength | | ISO 178 | 180to210 MPa |
| compression stress | | ISO 604 | 200to250 MPa |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| relative permittivity | 1MHz | IEC 60250 | 4.006.00 |
| Dissipation Factor | 100Hz | IEC 60250 | 0.010to0.020 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.020to0.040 |
| arc resistance | | ASTM D495 | PLC 4 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 2 |
| Surface Resistivity | | IEC 60093 | 1.0E+14到1.0E+15 ohms |
| Volume resistivity | | IEC 60093 | 1.0E+15到1.0E+16 ohms·cm |
| dielectric strength | | IEC 60243-1 | 20to30 kV/mm |
| relative permittivity | 100Hz | IEC 60250 | 4.006.00 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | >200 °C |
| Heat distortion temperature | 8.0MPa,未退火，HDT | ISO 75-2/C | 180to200 °C |
| Linear coefficient of thermal expansion | MD：50到150°C | ISO 11359-2 | 1.5E-5到2.0E-5 cm/cm/°C |
| thermal conductivity | | ASTME1461 | 0.40to0.60 W/m/K |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.
مقایسه