impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	30	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	45	kJ/m²
flammability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Burning wire flammability index	1.5mm	IEC 60695-2-12	700	°C
Flammability level	3.0mm	IEC 60695-11-10,-20	HB
Flammability level	Flammability level	1.5mm	IEC 60695-11-10,-20	HB
Burning rate	2.00mm	ISO 3795	20	mm/min
Hot filament ignition temperature	3.0mm	IEC 60695-2-13	725	°C
Hot filament ignition temperature	Hot filament ignition temperature	1.5mm	IEC 60695-2-13	725	°C
Burning wire flammability index	3.0mm	IEC 60695-2-12	700	°C
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Tensile strain	Break	ISO 527-2/1A/5	2.6	%
tensile strength	Break	ISO 527-2/1A/5	96.0	Mpa
Tensile modulus		ISO 527-2/1A/1	6500	Mpa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Vicat softening temperature	--	ISO 306/B50	145	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/A50	205	°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/Af	172	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/Bf	210	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Melt Volume Flow Rate (MVR)	250°C/2.16kg	ISO 1133	20.0	cm3/10min