ABS 266
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Shrinkage rate | ASTM D-955 | 0.40-0.60 % | |
| density | ASTM D-792 | 1.08 g/cm3 |
| Basic performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| melt mass-flow rate | 230℃,3.8kg | ASTM D-1238 | 5.0 g/10min |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Tensile modulus | ASTM D-638 | 1970 MPa | |
| tensile strength | 屈服 | ASTM D-638 | 37.2 MPa |
| 断裂 | ASTM D-638 | 29.0 MPa | |
| elongation at yield | ASTM D-638 | 4.0 % | |
| elongation | Break | ASTM D-638 | 48 % |
| Flexural modulus | ASTM D-790 | 1770 MPa | |
| bending strength | 屈服 | ASTM D-790 | 58.6 MPa |
| Impact strength of cantilever beam gap | 23℃,3.18mm | ASTM D-256 | 176 J/m |
| Rockwell hardness | ASTM D-785 | 108 R scale |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa，未退火，3.18mm，HDT | ASTM D-648 | 86.7 ℃ |
| Linear coefficient of thermal expansion | ASTM D-696 | 0.00012 cm/cm℃ | |
| combustibility | 1.50mm | HB UL 94 | |
| Heat distortion temperature | 0.45MPa，未退火，12.7mm，HDT | ASTM D-648 | 93.9 ℃ |
| 1.80MPa，未退火，3.18mm，HDT | ASTM D-648 | 72.8 ℃ | |
| 1.80MPa，未退火，12.7mm，HDT | ASTM D-648 | 82.2 ℃ |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.