PBT POCAN® KU 2-7604 000000 LANXESS GERMANY

توصیف محصول

گواهی‌نامه‌ها(0)

جدول خواص

توصیف محصول

گواهی‌نامه‌ها

No Data...

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	15	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	60	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	15	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	50	kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	NoBreak
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	NoBreak
flammability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
UL flame retardant rating	0.8mm	UL 94	V-0
Burning wire flammability index	0.8mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	0.8mm	IEC 60695-2-13	775	°C
	Hot filament ignition temperature	1.6mm	IEC 60695-2-13	775	°C
	Hot filament ignition temperature	Hot filament ignition temperature	3.0mm	IEC 60695-2-13	775	°C
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Nominal tensile fracture strain	23°C	ISO 527-2/50	>20	%
Bending modulus	23°C	ISO 178/A	2000	MPa
bending strength	3.5%Strain,23°C	ISO 178/A	65.0	MPa
bending strength	bending strength	23°C4	ISO 178/A	70.0	MPa
Bending strain	23°C	ISO 178/A	5.0	%
Tensile modulus	23°C	ISO 527-2/1	2000	MPa
tensile strength	Yield,23°C	ISO 527-2/50	45.0	MPa
Tensile strain	Yield,23°C	ISO 527-2/50	3.5	%
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	100	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	75.0	°C
Vicat softening temperature		ISO 306/B120	115	°C
Melting temperature		ISO 11357-3	225	°C
Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	1E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	1.1E-04	cm/cm/°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Apparent density		ISO 60	0.80	g/cm³
Melt Volume Flow Rate (MVR)	260°C/5.0kg	ISO 1133	20.0	cm³/10min
Shrinkage rate	TD:250°C,2.00mm2	ISO 2577	0.80	%
	Shrinkage rate	TD:120°C,4hr,2.00mm3	ISO 2577	0.80	%
		Shrinkage rate	MD:250°C,2.00mm2	ISO 2577	0.80	%
		Shrinkage rate	Shrinkage rate	MD:120°C,4hr,2.00mm3	ISO 2577	0.80	%
Water absorption rate	Saturation,23°C	ISO 62	0.30	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.10	%
density	23°C	ISO 1183	1.30	g/cm³
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 0
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Ball Pressure Test		ISO 2039-1	93.0	MPa
Supplementary Information	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
ISO Shortcut		ISO 7792	PBT+PC,GFHLMPR,11-020