physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
density | 23°C | ISO 1183 | 1.21 g/cm³ |
melt mass-flow rate | 280°C/5.0kg | ISO 1133 | 35 g/10min |
Shrinkage rate | 23°C | ISO 294-4 | 0.70to1.1 % |
Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Charpy Notched Impact Strength | -30°C | ISO 179 | 17 kJ/m² |
Charpy Notched Impact Strength | 23°C | ISO 179 | 8.1 kJ/m² |
Impact strength of simply supported beam without notch | -30°C | ISO 179 | 6.4 kJ/m² |
Impact strength of simply supported beam without notch | 23°C | ISO 179 | 97 kJ/m² |
Impact strength of cantilever beam gap | -30°C | ISO 180 | 7.2 kJ/m² |
Impact strength of cantilever beam gap | 23°C | ISO 180 | 16 kJ/m² |
Suspended wall beam without notch impact strength | -30°C | ISO 180 | 5.6 kJ/m² |
Suspended wall beam without notch impact strength | 23°C | ISO 180 | 96 kJ/m² |
Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
tensile strength | | ISO 527-2/50 | 100 MPa |
Tensile strain | Break | ISO 527-2/50 | 4.5 % |
Flexural modulus | 64.0mm | ISO 178 | 5000 MPa |
bending strength | 64.0mm | ISO 178 | 160 MPa |
Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Surface Resistivity | | IEC 60093 | 1E+15 ohms |
Volume resistivity | | IEC 60093 | 1E+15 ohms·cm |
Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
vicat | | ISO 306/B50 | 230 °C |