PC+AS T90 MF-20 Covestro - Polycarbonates

ویژگی‌ها:
Filler mineral filler 20% filler by weight
مقایسه

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of cantilever beam gap	-30°C	ISO 180/A	6.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/A	20 kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180	50 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180	100 kJ/m²

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
UL flame retardant rating	0.9mm	UL 94	HB

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus	23°C	ISO 527-2/1	4900 MPa
tensile strength	Yield,23°C	ISO 527-2/50	60.0 MPa
tensile strength	tensile strength	Break,23°C	ISO 527-2/50	50.0 MPa
Tensile strain	Yield,23°C	ISO 527-2/50	3.2 %
Tensile strain	Tensile strain	Break,23°C	ISO 527-2/50	9.0 %

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Vicat softening temperature	--	ISO 306/B120	130 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	111 °C
Vicat softening temperature	--	ISO 306/B50	128 °C
Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	4E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	5.6E-05 cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	127 °C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
density	23°C	ISO 1183	1.29 g/cm³
Melt Volume Flow Rate (MVR)	260°C/5.0kg	ISO 1133	12.0 cm³/10min
Shrinkage rate	TD:260°C,3.00mm	ISO 2577	0.25to0.45 %
Shrinkage rate	Shrinkage rate	MD:260°C,3.00mm	ISO 2577	0.30to0.50 %
Water absorption rate	Saturation,23°C	ISO 62	0.50 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.20 %
MeltViscosity	260°C	ISO 11443-A	240 Pa·s

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Surface resistivity		IEC 60093	1E+16 ohms
Volume resistivity	23°C	IEC 60093	1E+16 ohms·cm
Dielectric strength	23°C,1.00mm	IEC 60243-1	35 kV/mm
Relative permittivity	23°C,100Hz	IEC 60250	3.30
Relative permittivity	Relative permittivity	23°C,1MHz	IEC 60250	3.20
Dissipation factor	23°C,100Hz	IEC 60250	1.5E-03
Dissipation factor	Dissipation factor	23°C,1MHz	IEC 60250	3.2E-03
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 3