GPPS F664
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D-792 | 1.12 g/cm | |
| Shrinkage rate | Flow | ASTM D-955 | 0.40-0.70 % |
| Basic performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| melt mass-flow rate | 200℃,5kg | ASTM D-1238 | 7.0 g/10min |
| Water absorption rate | 24hr | ASTM D-570 | 0.050 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| tensile strength | ASTM D-638 | 26.5 MPa | |
| elongation at break | ASTM D-638 | 35 % | |
| Flexural modulus | ASTM D-790 | 2060 MPa | |
| bending strength | ASTM D-790 | 44.1 MPa | |
| Impact strength of cantilever beam gap | ASTM D-256 | 118 J/m | |
| Rockwell hardness | ASTM D-785 | 70 L scale |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Volume resistivity | ASTM D-257 | 1E-17 ohm.cm | |
| dielectric constant | ASTM D-150 | 2.500 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa，未退火，6.40mm，HDT | ASTM D-648 | 78.0 ℃ |
| vicat | Loading 1(10N) | ASTM D-1525 | 97.0 ℃ |
| Loading 2(50N) | ASTM D-1525 | 85.0 ℃ | |
| combustibility | 1.59mm,ALL | UL 94 | V-2 |
| 3.17mm,ALL | UL 746 | V-1 |