PA66 Vydyne® 20NSP
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ISO 1183 | 1.14 g/cm³ | |
| Shrinkage rate | TD:23°C,2.00mm | ISO 294-4 | 1.6 % |
| MD:23°C,2.00mm | ISO 294-4 | 1.4 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 1.2 % |
| 平衡,23°C,50%RH | ISO 62 | 2.4 % | |
| Outdoor applicability | UL 746C | f2 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Hot filament ignition temperature | 0.40mm | IEC 60695-2-13 | 825 °C |
| 0.71mm | IEC 60695-2-13 | 850 °C | |
| 1.5mm | IEC 60695-2-13 | 850 °C | |
| 3.0mm | IEC 60695-2-13 | 850 °C | |
| Limiting Oxygen Index | ISO 4589-2 | 26 % | |
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | 0.40mm | UL 94 | V-2 |
| 0.71mm | UL 94 | V-2 | |
| 1.5mm | UL 94 | V-2 | |
| 3.0mm | UL 94 | V-2 | |
| Burning wire flammability index | 0.40mm | IEC 60695-2-12 | 960 °C |
| 0.71mm | IEC 60695-2-12 | 960 °C | |
| 1.5mm | IEC 60695-2-12 | 960 °C |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| tensile strength | 断裂,23°C | ISO 527-2 | 75.0 MPa |
| Tensile strain | 屈服,23°C | ISO 527-2 | 5.0 % |
| Nominal tensile fracture strain | 23°C | ISO 527-2 | 13 % |
| Flexural modulus | 23°C | ISO 178 | 3200 MPa |
| bending strength | 23°C | ISO 178 | 100 MPa |
| Poisson's ratio | ISO 527-2 | 0.40 | |
| Tensile modulus | 23°C | ISO 527-2 | 3800 MPa |
| tensile strength | 屈服,23°C | ISO 527-2 | 95.0 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
| Impact strength of cantilever beam gap | -30°C | ISO 180 | 5.0 kJ/m² |
| 23°C | ISO 180 | 6.0 kJ/m² | |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 5.0 kJ/m² |
| 23°C | ISO 179/1eA | 6.0 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| High arc combustion index (HAI) | 1.5mm | UL 746 | PLC 0 |
| 3.0mm | UL 746 | PLC 0 | |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 0 |
| Hot wire ignition (HWI) | 0.40mm | UL 746 | PLC 4 |
| Volume resistivity | 0.750mm | IEC 60093 | 1E+13 ohms·cm |
| dielectric strength | 1.00mm | IEC 60243 | 26 kV/mm |
| arc resistance | 3.00mm | ASTM D495 | PLC 5 |
| Compared to the Leakage Tracking Index (CTI) | 3.00mm | IEC 60112 | PLC 0 |
| High arc combustion index (HAI) | 0.40mm | UL 746 | PLC 1 |
| 0.71mm | UL 746 | PLC 0 | |
| Hot wire ignition (HWI) | 0.71mm | UL 746 | PLC 4 |
| 1.5mm | UL 746 | PLC 3 | |
| 3.0mm | UL 746 | PLC 2 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| 线性热膨胀系数 | TD：23to55°C,2.00mm | ISO 11359-2 | 1E-04 cm/cm/°C |
| RTI Elec | 0.40mm | UL 746 | 130 °C |
| 0.71mm | UL 746 | 130 °C | |
| 1.5mm | UL 746 | 130 °C | |
| 3.0mm | UL 746 | 130 °C | |
| RTI Imp | 0.40mm | UL 746 | 75.0 °C |
| Hot deformation temperature (HDT) | 0.45MPa,未退火，HDT | ISO 75-2/B | 230 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 90.0 °C | |
| melting temperature | ISO 11357-3 | 260 °C | |
| 线性热膨胀系数 | MD：23to55°C,2.00mm | ISO 11359-2 | 1E-04 cm/cm/°C |
| RTI Imp | 0.71mm | UL 746 | 75.0 °C |
| 1.5mm | UL 746 | 75.0 °C | |
| 3.0mm | UL 746 | 75.0 °C | |
| RTI Str | 0.40mm | UL 746 | 75.0 °C |
| 0.71mm | UL 746 | 85.0 °C | |
| 1.5mm | UL 746 | 85.0 °C | |
| 3.0mm | UL 746 | 85.0 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.