PA6 TYLON® 235 TYNE USA
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Shrinkage rate | MD：3.18mm | ASTM D955 | 1.0to1.4 % |
| Water absorption rate | 24hr | ASTM D570 | 1.6 % |
| density | ASTM D792 | 1.13 g/cm³ | |
| ASTM D792 | 1.13 g/cm3 | ||
| Shrinkage rate | 3.18mm | ASTM D955 | 1.0-1.4 % |
| Water absorption rate | 24hr | ASTM D570 | 1.6 % |
| Rockwell hardness | R-Scale | ASTM D785 | 115 |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Rockwell hardness | R-Scale | ASTM D785 | 115 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Flexural modulus | ASTM D790 | 2760 MPa | |
| bending strength | ASTM D790 | 110 MPa | |
| tensile strength | ASTM D638 | 75.8 MPa | |
| elongation | Break | ASTM D638 | 80 % |
| tensile strength | ASTM D638 | 75.8 MPa | |
| elongation | Break | ASTM D638 | 80 % |
| Flexural modulus | ASTM D790 | 2760 MPa | |
| bending strength | ASTM D790 | 110 MPa | |
| Impact strength of cantilever beam gap | 6.35mm | ASTM D256 | 59 J/m |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Impact strength of cantilever beam gap | 6.35mm | ASTM D256 | 59 J/m |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 177 °C |
| 1.8MPa,未退火，HDT | ASTM D648 | 60.0 °C | |
| 0.45MPa,未退火，HDT | ASTM D648 | 177 ℃ | |
| 1.8MPa,未退火，HDT | ASTM D648 | 60.0 ℃ |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.