PA6 Staramide B28 EUROSTAR FRANCE

توصیف محصول

گواهی‌نامه‌ها(0)

جدول خواص

توصیف محصول

گواهی‌نامه‌ها

No Data...

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	4.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	5.0	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	>100	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	>270	kJ/m²
Impact strength of cantilever beam gap	-40°C	ISO 180/1A	3.0	kJ/m²
	Impact strength of cantilever beam gap	-20°C	ISO 180/1A	4.0	kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	5.0	kJ/m²
flammability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
UL flame retardant rating	0.75mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	HB
Burning wire flammability index	2.0mm	IEC 60695-2-12	960	°C
Extreme Oxygen Index		ISO 4589-2	24	%
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Tensile modulus		ISO 527-2/1	2700	MPa
tensile strength	Yield	ISO 527-2/50	70.0	MPa
elongation	Yield3	ASTM D638	3.5	%
elongation	elongation	Break	ISO 527-2/50	>15	%
Bending modulus		ISO 178	2400	MPa
bending strength		ISO 178	85.0	MPa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
RTI Imp		UL 746	65.0	°C
RTI		UL 746	65.0	°C
Vicat softening temperature	--	ISO 306/B50	210	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	200	°C
Ball Pressure Test	125°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	MD:23to60°C	ISO 11359-2	8E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:23to60°C	ISO 11359-2	8E-05	cm/cm/°C
thermal conductivity		ISO 8302	0.29	W/m/K
RTI Elec		UL 746	65.0	°C
Hot deformation temperature	1.8MPa,Unannealed,100mmSpan	ISO 75-2/Ae	60.0	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,100mmSpan	ISO 75-2/Be	180	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
density		ISO 1183	1.14	g/cm³
Shrinkage rate	MD	Internal Method	1.1to1.5	%
Water absorption rate	Saturation,23°C	ISO 62	10	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	2.6	%
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Surface resistivity		IEC 60093	>1.0E+16	ohms
Dissipation factor	60Hz	IEC 60250	5.8E-03
Dissipation factor	Dissipation factor	1MHz	IEC 60250	0.018
Compared to the anti leakage trace index	--	IEC 60112	PLC 0
Compared to the anti leakage trace index	Compared to the anti leakage trace index	SolutionB	IEC 60112	PLC 0
Volume resistivity		IEC 60093	>1.0E+16	ohms·cm
Dielectric strength	3.20mm,in Oil	IEC 60243-1	16	kV/mm
Relative permittivity	50Hz	IEC 60250	3.30
	Relative permittivity	60Hz	IEC 60250	3.30
	Relative permittivity	Relative permittivity	1MHz	IEC 60250	3.00
Dissipation factor	50Hz	IEC 60250	5.8E-03
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Rockwell hardness	R-Sale	ISO 2039-2	120

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.