PP r-PP51 0000 Axion Polymers
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| flow | mm/mm | 71.1E-3-228.6E-3 | |
| lateral flow | mm/mm | 226.1E-3-0.330 | |
| density | -- | 1.12to1.28 | |
| flow | mm/mm | 71.1E-3-228.6E-3 | |
| density | -- | 1.12to1.28 | |
| lateral flow | mm/mm | 226.1E-3-0.330 |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Rockwell hardness | 23℃ | 100to110 | |
| Shore hardness | 23℃ | 74to79 | |
| Rockwell hardness | 23℃ | 100to110 | |
| Shore hardness | 23℃ | 74to79 |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Charpy Notched Impact Strength | 23℃ | kJ/m² | 0.882to1.811 |
| Dart impact | 23℃ | N.m | 17.70to66.19 |
| Impact strength of cantilever beam gap | 23℃ | J/m | 0.012to0.037 |
| Suspended wall beam without notch impact strength | 23℃ | J/m | 0.066to0.151 |
| Charpy Notched Impact Strength | 23℃ | kJ/m² | 0.882to1.811 |
| Dart impact | 23℃ | N.m | 17.70to66.19 |
| Impact strength of cantilever beam gap | 23℃ | J/m | 0.012to0.037 |
| Suspended wall beam without notch impact strength | 23℃ | J/m | 0.066to0.151 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| yield | 27.59to93.79 Mpa | ||
| 27.59to93.79 Mpa | |||
| elongation | 断裂,23℃ | % | 2.9to5.1 |
| 断裂,23℃ | % | 2.9to5.1 |