PC XANTAR® 27 R Mitsubishi Chemical Corporation

مقایسه

برگه داده فنی

optical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
transmissivity		ASTM D1003	89.0 %

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of cantilever beam gap	23°C	ISO 180/4A	80 kJ/m²

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
UL flame retardant rating	3.0mm	IEC 60695-11-10,-20	V-2
Burning wire flammability index	3.0mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	1.5mm	IEC 60695-2-13	825 °C
Hot filament ignition temperature	Hot filament ignition temperature	3.0mm	IEC 60695-2-13	875 °C
Extreme Oxygen Index		ISO 4589-2	26 %
UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	V-2
Burning wire flammability index	1.5mm	IEC 60695-2-12	800 °C

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	Yield	ISO 527-2	60.0 MPa
Tensile strain	Yield	ISO 527-2	6.0 %
Nominal tensile fracture strain		ISO 527-2	>50 %
Bending modulus		ISO 178	2400 MPa
bending strength		ISO 178	90.0 MPa
Tensile modulus		ISO 527-2	2300 MPa

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Linear coefficient of thermal expansion	MD	ISO 11359-2	6.5E-05 cm/cm/°C
RTI Elec	1.5mm	UL 746	130 °C
RTI Elec	RTI Elec	3.0mm	UL 746	130 °C
RTI Imp	1.5mm	UL 746	125 °C
RTI Imp	RTI Imp	3.0mm	UL 746	130 °C
RTI Str	1.5mm	UL 746	125 °C
RTI Str	RTI Str	3.0mm	UL 746	130 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	130 °C
Vicat softening temperature		ISO 306/B50	150 °C
Ball Pressure Test	125°C	IEC 60695-10-2	Pass

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
ThermalConductivityofMelt			0.24 W/m/K
density		ISO 1183	1.20 g/cm³
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	3.00 cm³/10min
Shrinkage rate	MD	ISO 294-4	0.60 %
Water absorption rate	Saturation,23°C	ISO 62	0.35 %
LimitingViscosity		ISO 1628-4	61.0 cm³/g

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Surface resistivity		IEC 60093	>1.0E+15 ohms
Compared to the anti leakage trace index	CTI	UL 746	PLC 2
Compared to the anti leakage trace index	Compared to the anti leakage trace index		IEC 60112	PLC 3
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm
Dielectric strength		IEC 60243-1	29 kV/mm
Relative permittivity	100Hz	IEC 60250	3.00
Relative permittivity	Relative permittivity	1MHz	IEC 60250	2.90
Dissipation factor	100Hz	IEC 60250	6.6E-04
Dissipation factor	Dissipation factor	1MHz	IEC 60250	9.2E-03

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Rockwell hardness	M-Scale	ISO 2039-2	70