impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Impact strength of cantilever beam gap	23°C	ISO 180/1A	3.5	kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	15	kJ/m²
Dart impact	23°C,EnergyatPeakLoad	ASTM D3763	4.80	J
Multi axis Instrumented Impact Energy		ISO 6603-2	1.60	J
flammability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
UL flame retardant rating	1.5mm	UL 94	V-0
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Tensile modulus		ASTM D638	4140	Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	3620	Mpa
tensile strength	Yield	ASTM D638	42.1	Mpa
	tensile strength	Yield	ISO 527-2	43.0	Mpa
		tensile strength	Break	ASTM D638	42.1	Mpa
		tensile strength	tensile strength	Break	ISO 527-2	42.0	Mpa
elongation	Yield	ASTM D638	1.8	%
Tensile strain	Yield	ISO 527-2	1.8	%
elongation	Break	ASTM D638	1.9	%
Tensile strain	Break	ISO 527-2	1.9	%
Bending modulus		ASTM D790	3450	Mpa
Bending modulus	Bending modulus		ISO 178	3200	Mpa
bending strength		ASTM D790	55.2	Mpa
bending strength	bending strength		ISO 178	61.0	Mpa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	96.7	°C
	Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	98.0	°C
		Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	87.2	°C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	90.0	°C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	9.4E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	9.4E-05	cm/cm/°C
		Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	6.1E-05	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	6.2E-05	cm/cm/°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Shrinkage rate	MD：24hr	ASTM D955	0.80-1.0	%
	Shrinkage rate	TD：24hr	ASTM D955	0.90-1.1	%
		Shrinkage rate	TD:24hr	ISO 294-4	1.0	%
		Shrinkage rate	Shrinkage rate	MD:24hr	ISO 294-4	0.93	%
Water absorption rate	24hr,50%RH	ASTM D570	2.0	%
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Surface resistivity		ASTM D257	1.0E+10to1.0E+12	ohms