برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| melt mass-flow rate | | ASTM D1238 | 3.0 g/10min |
| Shrinkage rate | MD | ASTM D955 | 0.20to0.50 % |
| density | | ASTM D792 | 1.15 g/cm³ |
| Apparent density | | ASTM D1895 | 0.66 g/cm³ |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | M-Scale | ASTM D785 | 60 |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Haze ratio | 254µm | ASTM D1003 | 2.7 % |
| Yellowness Index | 0.254mm | ASTM D1925 | 2.5 YI |
| gloss | 60°,254µm | ASTM D2457 | 120 |
| transmissivity | 254µm | ASTM D1003 | 92.5 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Flexural modulus | | ASTM D790 | 3380 MPa |
| bending strength | Yield | ASTM D790 | 96.5 MPa |
| tensile strength | Yield | ASTM D638 | 65.5 MPa |
| elongation | Yield | ASTM D638 | 3.0 % |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 270 J/m |
| film | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| OTr | 23°C,100%RH | ASTM D3985 | 0.31 cm³·mm/m²/atm/24hr |
| Water Vapor Transmission Rate | | ASTMF1249 | 2.0 g·mm/m²/atm/24hr |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 76.7 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 68.9 °C |
| Linear coefficient of thermal expansion | MD：20到80°C | ASTM D696 | 6.7E-05 cm/cm/°C |
| specific heat | 20°C | ASTMC351 | 1340 J/kg/°C |
| thermal conductivity | | ASTMC177 | 0.25 W/m/K |