physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Water absorption rate | | GB/T2914 | 0.02 % |
Water absorption rate | | GB/T2914 | 0.02 % |
Water absorption rate | | GB/T2914 | 0.02 % |
Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
tensile strength | | GB/T1040 | 200 Mpa |
elongation at break | | GB/T1040 | 1.8 % |
bending strength | | GB/T9341 | 280 Mpa |
Flexural modulus | | GB/T9341 | 1.4×10⁴ Mpa |
Impact strength of cantilever beam gap | | GB/T1843 | 13 kJ/m² |
tensile strength | | GB/T1040 | 200 Mpa |
elongation at break | | GB/T1040 | 1.8 % |
bending strength | | GB/T9341 | 280 Mpa |
Flexural modulus | | GB/T9341 | 1.4×10⁴ Mpa |
Impact strength of cantilever beam gap | | GB/T1843 | 13 kJ/m² |
tensile strength | | GB/T1040 | 200 Mpa |
elongation at break | | GB/T1040 | 1.8 % |
bending strength | | GB/T9341 | 280 Mpa |
Flexural modulus | | GB/T9341 | 1.4×10⁴ Mpa |
Impact strength of cantilever beam gap | | GB/T1843 | 13 kJ/m² |
Physical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
density | | GB/T1033 | 1.66 g/cm³ |
Mold Shrinkage | | GB/T15585 | 0.25/0.75 % |
density | | GB/T1033 | 1.66 g/cm³ |
Mold Shrinkage | | GB/T15585 | 0.25/0.75 % |
density | | GB/T1033 | 1.66 g/cm³ |
Mold Shrinkage | | GB/T15585 | 0.25/0.75 % |
Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Volume resistivity | | | 5 ×10¹⁵Ω·M |
Surface Resistivity | | | 5 ×10¹⁴Ω |
dielectric constant | | | 4 1MHz |
electric strength | | GB/T1408 | 20 KV/mm |
Volume resistivity | | | 5 ×10¹⁵Ω·M |
Surface Resistivity | | | 5 ×10¹⁴Ω |
dielectric constant | | | 4 1MHz |
electric strength | | GB/T1408 | 20 KV/mm |
Volume resistivity | | | 5 ×10¹⁵Ω·M |
Surface Resistivity | | | 5 ×10¹⁴Ω |
dielectric constant | | | 4 1MHz |
electric strength | | GB/T1408 | 20 KV/mm |
Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
melting point | | GB/T4608 | 285 °C |
Heat distortion temperature | 1.8MPa | GB/T1634 | 267 °C |
Flame retardancy | | GB/TUL94 | V-0 |
melting point | | GB/T4608 | 285 °C |
Heat distortion temperature | 1.8MPa | GB/T1634 | 267 °C |
Flame retardancy | | GB/TUL94 | V-0 |
melting point | | GB/T4608 | 285 °C |
Heat distortion temperature | 1.8MPa | GB/T1634 | 267 °C |
Flame retardancy | | GB/TUL94 | V-0 |