PVOH MonoSol® AF L337 MonoSol, LLC

مقایسه

برگه داده فنی

physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
water content	23°C		7.6 wt%
solubility	Disintegration:10°C,50.0µm		24.0 sec
	solubility	Disintegration:24°C,50.0µm		12.0 sec
		solubility	Dissolution:10°C,50.0µm		83.0 sec
		solubility	solubility	Dissolution:24°C,50.0µm		58.0 sec

film	شرایط آزمون	روش آزمون	نتیجه آزمون
film thickness			50 µm
film thickness	film thickness			20µmto60µm
Secant modulus	10%,MD:50µm	ASTMD882	49.6 MPa
	Secant modulus	100%,MD:50µm	ASTMD882	17.2 MPa
		Secant modulus	10%,TD:50µm	ASTMD882	43.4 MPa
		Secant modulus	Secant modulus	100%,TD:50µm	ASTMD882	8.96 MPa
tensile strength	MD:断裂,50µm	ASTM D882	30.3 MPa
	tensile strength	TD:断裂,50µm	ASTM D882	31.7 MPa
		tensile strength	MD:50µm	ISO 527-3	30.3 MPa
		tensile strength	tensile strength	TD:50µm	ISO 527-3	31.7 MPa
elongation	TD:断裂,50µm	ISO 527-3	420 %
Elmendorf tear strength	MD:50µm	ASTM D1922	1300 g
Elmendorf tear strength	Elmendorf tear strength	TD:50µm	ASTM D1922	1500 g
elongation	MD:断裂,50µm	ASTMD882	230 %
elongation	elongation	TD:断裂,5.0E-3µm	ASTM D882	420 %
Elmendorf tear strength	MD:50µm	ISO 6383-2	0.13 N
Elmendorf tear strength	Elmendorf tear strength	TD:50µm	ISO 6383-2	0.15 N
usage	50.0µm	ASTM D4321	16.1 m²/kg