| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792 | 1.03 g/cm³ |
| melt mass-flow rate | 200℃/5.0 kg | ASTM D1238 | 1.8 g/10 min |
| melt mass-flow rate | 220℃/10.0 kg | ASTM D1238 | 18 g/10 min |
| Shrinkage rate | MD | ASTM D955 | < 0.40 % |
| Water absorption rate | 饱和 | ASTM D570 | < 0.30 % |
| density | | ASTM D792 | 1.03 g/cm³ |
| melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 1.8 g/10min |
| melt mass-flow rate | 220°C/10.0kg | ASTM D1238 | 18 g/10min |
| Shrinkage rate | MD | ASTM D955 | <0.40 % |
| Water absorption rate | 饱和 | ASTM D570 | <0.30 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | R计秤,23°C | ASTM D785 | 110 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| bending strength | 屈服, 23℃ | ASTM D790 | 68.9 Mpa |
| Impact strength of cantilever beam gap | 23℃, 3.18 mm | ASTM D256 | 260 J/m |
| Impact strength of cantilever beam gap | 23℃, 6.35 mm | ASTM D256 | 230 J/m |
| Rockwell hardness | R 级, 23℃ | ASTM D785 | 110 |
| tensile strength | 屈服, 23℃, 3.18 mm | ASTM D638 | 40 Mpa |
| tensile strength | 断裂, 23℃, 3.18 mm | ASTM D638 | 35.2 Mpa |
| elongation | 断裂, 23℃, 3.18 mm | ASTM D638 | 30 % |
| Flexural modulus | 23℃ | ASTM D790 | 2340 Mpa |
| Flexural modulus | 23°C | ASTM D790 | 2340 Mpa |
| bending strength | 屈服,23°C | ASTM D790 | 68.9 Mpa |
| tensile strength | 屈服,23°C,3.18mm | ASTM D638 | 40.0 Mpa |
| tensile strength | Break,23°C,3.18mm | ASTM D638 | 35.2 Mpa |
| elongation | 断裂,23°C,3.18mm | ASTM D638 | 30 % |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | 23°C,3.18mm | ASTM D256 | 260 J/m |
| Impact strength of cantilever beam gap | 23°C,6.35mm | ASTM D256 | 230 J/m |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| High arc combustion index (HAI) | 1.57mm | UL 746 | |
| High Voltage Arc Traceability Rate (HVTR) | 1.57mm | UL 746 | mm/min |
| Hot wire ignition (HWI) | 1.57mm | UL 746 | sec |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8 MPa, 退火, 12.7 mm，HDT | ASTM D648 | 86 °C |
| vicat | | ASTM D1525 | 103 °C |
| High arc combustion index (HAI) | 1.57 mm | UL 746 | |
| High Voltage Arc Traceability Rate (HVTR) | 1.57 mm | UL 746 | mm/min |
| Hot wire ignition (HWI) | 1.57 mm | UL 746 | sec |
| UL flame retardant rating | 1.59 mm | UL 94 | HB |
| Heat distortion temperature | 1.8MPa,Annealed,12.7mm，HDT | ASTM D648 | 86.0 °C |
| vicat | | ASTM D15255 | 103 °C |
| RTI Elec | 1.6mm | UL 746 | 60.0 °C |
| RTI Imp | 1.6mm | UL 746 | 60.0 °C |
| RTI Str | 1.6mm | UL 746 | 60.0 °C |