optical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Refractive index		ASTMD542	1.586
transmissivity		ASTM D1003	89.0	%
turbidity		ASTM D1003	1.0	%
impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Dart impact	23°C,总能量	ASTM D3763	81.3	J
Impact strength of cantilever beam gap		ASTM D1822	378	kJ/m²
Charpy Notched Impact Strength	-30°C	SK	无断裂
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	SK	无断裂
Suspended wall beam without notch impact strength	23°C	ASTMD256	无断裂
flammability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Normal combustion performance with a thickness of 1.6mm	1.60mm,UL	ISO 12104	HB
UL flame retardant rating	3.20mm	ISO 12104	HB
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
tensile strength	Break5	ASTM D638	68.3	Mpa
tensile strength	tensile strength	Break	ISO 527-2/50	68.0	Mpa
elongation	Yield5	ASTM D638	6.0	%
	elongation	Yield	ISO 527-2/50	6.0	%
		elongation	Break5	ASTM D638	150	%
			elongation	Break	ISO 527-2/50	150	%
			elongation	elongation	Break	ISO 527-24	>50	%
Bending modulus	--6	ASTM D790	2410	Mpa
Bending modulus	Bending modulus	--7,8	ISO 178	2400	Mpa
bending strength	--6	ASTM D790	96.5	Mpa
Tensile modulus	--5	ASTM D638	2210	Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/50	2300	Mpa
tensile strength	Yield5	ASTM D638	62.1	Mpa
tensile strength	tensile strength	Yield	ISO 527-2/50	62.0	Mpa
bending strength	--7,8	ISO 178	98.0	Mpa
Wear resistance		ASTM D1044	45	%
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot deformation temperature	0.45MPa,Annealed	ASTM D648	139	°C
	Hot deformation temperature	0.45MPa	ISO 75-24	137	°C
		Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	122	°C
			Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	120	°C
				Hot deformation temperature	1.8MPa,Annealed	ASTM D648	136	°C
				Hot deformation temperature	Hot deformation temperature	1.8MPa	ISO 75-24	123	°C
Vicat softening temperature	--	ASTM D152510	148	°C
	Vicat softening temperature	--	ISO 306/B50	143	°C
	Vicat softening temperature	Vicat softening temperature	50°C/h,B(50N)	ISO 3064	143	°C
Linear coefficient of thermal expansion	MD：-40to82°C	ASTM D696	6.8E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：--	ISO 178/1993	7E-05	cm/cm/°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 11334	12.0	cm3/10min
Shrinkage rate	MD	ASTM D955	0.50-0.70	%
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	0.50-0.70	%
Water absorption rate	23°C,24hr	ASTMD570	0.15	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ASTMD570	0.32	%
melt mass-flow rate	300°C/1.2kg	ASTMD1238	15	g/10min
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Volume resistivity	--	ASTM D257	2E+17	ohms·cm
Volume resistivity	Volume resistivity	--	IEC 600934	>1.0E+13	ohms·m
Dielectric strength		ASTMD1494	17	KV/mm
Dielectric constant	60Hz	ASTM D150	3.00
	Dielectric constant	1MHz	ASTMD150	3.00
	Dielectric constant	Dielectric constant	100Hz	IEC 602504	3.00
Dissipation factor	50Hz	ASTM D150	1E-03
	Dissipation factor	1MHz	ASTMD150	2E-03
	Dissipation factor	Dissipation factor	100Hz	IEC 602504	1E-03
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Rockwell hardness	R-Scale	ASTM D785	118