| شرایط آزمون | روش آزمون | نتیجه آزمون | |
|---|---|---|---|
| melt mass-flow rate | 230°C/2.16kg | ISO 1133 | 1.0 g/10min |
| Shrinkage rate | 23°C,24小时,3.18mm | ISO 294-4 | 0.90to1.2 % |
| tensile strength | 屈服,23°C | ISO 527-2 | 22.7 MPa |
| Linear coefficient of thermal expansion | MD：-30到100°C | ASTME831 | 9.9E-05 cm/cm/°C |
| density | ISO 1183 | 0.988 g/cm³ | |
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| gloss | 60°,3180µm,热塑,光滑 | ISO 2813 | 20to40 |
| HeatSag | 149°C,3.20mm | ASTM D3769 | 0.00 mm |
| Tensile strain | 断裂,233°C | ISO 527-2 | 700 % |
| Flexural modulus | 23°C | ISO 178 | 1720 MPa |
| Impact strength of cantilever beam gap | -30°C,3.18mm,注塑，流量 | ASTM D256 | 260 J/m |
| 23°C,3.18mm,注塑，流量 | ASTM D256 | NoBreak | |
| InstrumentedDartImpact | -30°C,TotalEnergy,DuctileFailure | ASTM D3763 | 47.5 J |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/Bf | 93.9 °C |