PVOH MonoSol® AF L711 MonoSol, LLC
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| water content | 23°C | 7.1 wt% | |
| solubility | Disintegration:10°C,35.0µm | 12.0 sec | |
| Disintegration:24°C,35.0µm | 5.0 sec | ||
| Dissolution:10°C,35.0µm | 120.0 sec | ||
| Dissolution:24°C,35.0µm | 72.0 sec |
| film | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Secant modulus | 10%,TD:36µm | ASTMD882 | 82.7 MPa |
| 100%,TD:36µm | ASTMD882 | 22.8 MPa | |
| tensile strength | MD:断裂,36µm | ASTM D882 | 45.5 MPa |
| TD:断裂,36µm | ASTM D882 | 43.4 MPa | |
| MD:36µm | ISO 527-3 | 45.5 MPa | |
| TD:36µm | ISO 527-3 | 43.4 MPa | |
| elongation | MD:断裂,36µm | ASTMD882 | 180 % |
| Elmendorf tear strength | TD:36µm | ISO 6383-2 | 0.040 N |
| usage | 35.0µm | ASTM D4321 | 22.9 m²/kg |
| film thickness | 20µmto60µm | ||
| Secant modulus | 10%,MD:36µm | ASTMD882 | 89.6 MPa |
| film thickness | 35 µm | ||
| elongation | TD:断裂,36µm | ASTMD882 | 230 % |
| Dart impact | 36µm | ASTMD1709 | 560 g |
| Elmendorf tear strength | MD:36µm | ASTM D1922 | 390 g |
| TD:36µm | ASTM D1922 | 390 g | |
| MD:36µm | ISO 6383-2 | 0.040 N | |
| Secant modulus | 100%,MD:36µm | ASTMD882 | 33.8 MPa |