| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ISO 1183 | 1.39 g/cm³ |
| Water absorption rate | 饱和,23°C | | 0.50 % |
| Water absorption rate | 平衡,23°C,50%RH | | 0.50 % |
| Water absorption rate | after24himmersioninwater:23°C | ISO 62 | 6.0 mg |
| Water absorption rate | after96himmersioninwater:23°C | ISO 62 | 13.0 mg |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | M计秤 | ISO 2039-2 | 96 |
| ball-indentation hardness | | ISO 2039-1 | 170 MPa |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 3.00mm | UL 94 | HB |
| UL flame retardant rating | 6.00mm | UL 94 | HB |
| Limiting Oxygen Index | | ISO 4589-2 | 25 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | 23°C | ISO 527-2 | 3700 MPa |
| tensile strength | 屈服,23°C | ISO 527-2 | 90.0 MPa |
| Tensile strain | 断裂,23°C | ISO 527-2 | 15 % |
| Tensile creep modulus | 1000hr | ISO 899-1 | 26.0 MPa |
| compression stress | 5%应变 | ISO 604 | 103 MPa |
| compression stress | 2%应变 | ISO 604 | 51.0 MPa |
| compression stress | 1%应变 | ISO 604 | 26.0 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 2.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | >50 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/2A | 2.0 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | IEC 60093 | >1.0E+14 ohms |
| Volume resistivity | | IEC 60093 | >1.0E+15 ohms·cm |
| dielectric strength | | IEC 60243-1 | 22 kV/mm |
| relative permittivity | 100Hz | IEC 60250 | 3.40 |
| relative permittivity | 1MHz | IEC 60250 | 3.20 |
| Dissipation Factor | 100Hz | IEC 60250 | 1E-03 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.014 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 75.0 °C |
| melting temperature | | | 255 °C |
| Linear coefficient of thermal expansion | MD：23到60°C | | 6E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | MD：23到100°C | | 8E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | MD：导热系数 | | 0.29 W/m/K |
| Linear coefficient of thermal expansion | MD：ServiceTemperature-Minimum | | -20 °C |
| maximum service temperature | inaircontinuosly | | 115 °C |
| maximum service temperature | inairforshortperiods | | 160 °C |