impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	60	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	75	kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	55	kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	60	kJ/m²
flammability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
UL flame retardant rating	0.75mm	UL 94	HB
	UL flame retardant rating	1.5mm	UL 94	HB
		UL flame retardant rating	1.6mm	UL 94	HB
			UL flame retardant rating	3.0mm	UL 94	HB
			UL flame retardant rating	UL flame retardant rating	3.2mm	UL 94	HB
Burning wire flammability index	0.8mm	IEC 60695-2-12	700	°C
	Burning wire flammability index	1.6mm	IEC 60695-2-12	700	°C
	Burning wire flammability index	Burning wire flammability index	3.0mm	IEC 60695-2-12	700	°C
Extreme Oxygen Index		ISO 4589-2	23	%
BurningBehavior	>1.00mm	ISO 3795	passed
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
bending strength	23°C	ASTM D790	270	Mpa
	bending strength	3.5%Strain	ISO 178/A	265	Mpa
		bending strength	23°C	ISO 178	270	Mpa
		bending strength	bending strength	FlexuralStrainatFlexuralStrength6(23°C)		4.0	%
Tensile modulus	23°C	ASTM D638	9170	Mpa
Tensile modulus	Tensile modulus	23°C	ISO 527-2/1	10000	Mpa
tensile strength	Break,23°C	ASTM D638	170	Mpa
tensile strength	tensile strength	Break,23°C	ISO 527-2/5	175	Mpa
elongation	Break,23°C	ASTM D638	3.0	%
Tensile strain	Break,23°C	ISO 527-2/5	3.0	%
Nominal tensile fracture strain	23°C	ISO 527-2/50	4.4	%
Bending modulus	23°C	ASTM D790	8690	Mpa
Bending modulus	Bending modulus	23°C	ISO 178/A	9200	Mpa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot deformation temperature	0.45MPa,Unannealed,4.00mm	ASTM D648	>249	°C
	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	250	°C
		Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ASTM D648	>249	°C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	>240	°C
Vicat softening temperature	--	ISO 306/B50	230	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	>230	°C
Ball Pressure Test	253°C	IEC 60695-10-2	Pass
Melting temperature		ISO 11357-3	263	°C
Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	3E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	9E-05	cm/cm/°C
RTI Elec	0.75mm	UL 746	125	°C
RTI Elec	RTI Elec	1.5mm	UL 746	125	°C
RTI Imp	0.75mm	UL 746	90.0	°C
RTI Imp	RTI Imp	1.5mm	UL 746	105	°C
RTI Str	0.75mm	UL 746	110	°C
RTI Str	RTI Str	1.5mm	UL 746	115	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Apparent density		ISO 60	0.70	g/cm³
Shrinkage rate	TD:290°C,2.00mm2	ISO 294-4	0.93	%
	Shrinkage rate	TD:120°C,2hr,2.00mm3	ISO 294-4	0.13	%
		Shrinkage rate	MD:290°C,2.00mm2	ISO 294-4	0.39	%
		Shrinkage rate	Shrinkage rate	MD:120°C,2hr,2.00mm3	ISO 294-4	0.070	%
Water absorption rate	Saturation,23°C	ISO 62	5.5	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	2.0	%
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Surface resistivity		IEC 60093	1E+15	ohms
Volume resistivity	23°C	IEC 60093	1E+15	ohms·cm
Dielectric strength	23°C,1.00mm	IEC 60243-1	35	KV/mm
Dielectric strength	Dielectric strength	23°C,3.00mm	IEC 60243-1	30	KV/mm
Dielectric constant	23°C,50Hz	IEC 60250	4.00
Dielectric constant	Dielectric constant	23°C,1MHz	IEC 60250	4.00
Relative permittivity	23°C,100Hz	IEC 60250	4.00
Relative permittivity	Relative permittivity	23°C,1MHz	IEC 60250	4.00
Dissipation factor	23°C,50Hz	IEC 60250	0.012
	Dissipation factor	23°C,100Hz	IEC 60250	0.012
	Dissipation factor	Dissipation factor	23°C,1MHz	IEC 60250	0.0190.019
Compared to the anti leakage trace index	SolutionA	IEC 60112		V
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Ball Pressure Test		ISO 2039-1	220	Mpa
film	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Thin film puncture strength	--7	ISO 6603-2	2.80	J
	Thin film puncture strength	--8	ISO 6603-2	2.30	J
		Thin film puncture strength	--7	ISO 6603-2	900	N
		Thin film puncture strength	Thin film puncture strength	--8	ISO 6603-2	800	N
Supplementary Information	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
ISO Shortcut		ISO 1874	PA66.GHR.14-100.GF30

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.