PBT POCAN® B 1701 000000 LANXESS GERMANY

توصیف محصول

گواهی‌نامه‌ها(0)

جدول خواص

توصیف محصول

گواهی‌نامه‌ها

No Data...

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	200	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	<10	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	<10	kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	无断裂
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	<10	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	<10	kJ/m²
flammability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
UL flame retardant rating	0.800mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	1.60mm	UL 94	HB
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Nominal tensile fracture strain	23°C	ISO 527-2/50	>20	%
Bending modulus	23°C	ISO 178/A	2500	MPa
Bending strain	23°C		6.0	%
Tensile modulus	23°C	ISO 527-2/1	2700	MPa
tensile strength	Yield,23°C	ISO 527-2/50	60.0	MPa
Tensile strain	Yield,23°C	ISO 527-2/50	9.0	%
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Linear coefficient of thermal expansion	MD:23to55°C	ISO 11359-2	1.2E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:23to55°C	ISO 11359-2	1.2E-04	cm/cm/°C
Vicat softening temperature		ISO 306/B120	180	°C
Melting temperature		ISO 11357-3	225	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Melt Volume Flow Rate (MVR)	260°C/2.16kg	ISO 1133	12.0	cm³/10min
Shrinkage rate	TD:260°C,2.00mm1	ISO 294-4	2.0	%
	Shrinkage rate	TD:120°C,2hr,2.00mm2	ISO 294-4	0.20	%
		Shrinkage rate	MD:260°C,2.00mm3	ISO 294-4	2.0	%
		Shrinkage rate	Shrinkage rate	MD:120°C,2hr,2.00mm4	ISO 294-4	0.20	%
Water absorption rate	Saturation,23°C	ISO 62	0.50	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.20	%
density	23°C	ISO 1183	1.31	g/cm³
Apparent density		ISO 60	0.80	g/cm³
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Relative permittivity	23°C,1MHz	IEC 60250	3.20
Dissipation factor	23°C,100Hz	IEC 60250	1.5E-03
Dissipation factor	Dissipation factor	23°C,1MHz	IEC 60250	0.020
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 0
Surface resistivity		IEC 60093	<1.0E+15	ohms
Volume resistivity	23°C	IEC 60093	>1.0E+15	ohms·cm
Dielectric strength	23°C,1.00mm	IEC 60243-1	30	kV/mm
Relative permittivity	23°C,100Hz	IEC 60250	3.40
Supplementary Information	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
ISO Shortcut		ISO 7792	PBT,GM,13-030