LLDPE UF 1810
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D1505 | 0.919 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 1.0 g/10min |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| gloss | 45°,30.0µm,吹塑薄膜 | ASTM D2457 | 72 |
| transparency | 30.0µm,吹塑薄膜 | ASTM D1746 | 75.0 |
| Haze ratio | 30.0µm,吹塑薄膜 | ASTM D1003 | 11 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| coefficient of friction | Blown Film | ASTM D1894 | 0.60 |
| film | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| tensile strength | TD:断裂,30µm,吹塑薄膜 | ASTM D882 | 24.0 MPa |
| elongation | MD:断裂,30µm,吹塑薄膜 | ASTM D882 | 700 % |
| TD:断裂,30µm,吹塑薄膜 | ASTM D882 | 850 % | |
| Dart impact | 30µm,吹塑薄膜 | ASTM D1709 | 100 g |
| Elmendorf tear strength | MD:30.0µm | ASTM D1922 | 24.5 kN/m |
| TD:30.0µm | ASTM D1922 | 196.1 kN/m | |
| film thickness | 30 µm | ||
| tensile strength | MD:断裂,30µm,吹塑薄膜 | ASTM D882 | 50.0 MPa |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| brittle temperature | ASTM D746 | <-70.0 °C | |
| vicat | ASTM D1525 | 104 °C |