برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ISO 1183 | 1.20 g/cm³ |
| Melt volume flow rate | 300°C/1.2 kg | ISO 1133 | 8.00 cm3/10min |
| Shrinkage rate | 横向流量 : 4.00 mm | 内部方法 | 0.50 - 0.70 % |
| Shrinkage rate | 流量 : 4.00 mm | 内部方法 | 0.50 - 0.70 % |
| Water absorption rate | 24 hr, 23°C | ISO 62 | 0.20 % |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| refractive index | | ASTM D542 | 1.585 |
| transmissivity | 3000 µm | ASTM D1003 | 88.0 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.5 mm | UL 94 | HB |
| UL flame retardant rating | 0.40 mm | UL 94 | V-2 |
| Burning wire flammability index | 1.5 mm | IEC 60695-2-12 | 825 °C |
| Burning wire flammability index | 3.0 mm | IEC 60695-2-12 | 875 °C |
| Hot filament ignition temperature | 1.5 mm | IEC 60695-2-13 | 850 °C |
| Hot filament ignition temperature | 3.0 mm | IEC 60695-2-13 | 850 °C |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | | ISO 527-2/1 | 2400 Mpa |
| tensile strength | 屈服 | ISO 527-2/50 | 61.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2/50 | 6.0 % |
| Nominal tensile fracture strain | | ISO 527-2/50 | > 50 % |
| Flexural modulus | | ISO 178 | 2350 Mpa |
| bending strength | | ISO 178 | 93.0 Mpa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | | ISO 179 | 76 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179 | 无断裂 |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | IEC 60093 | > 1.0E+15 ohms |
| Volume resistivity | | IEC 60093 | > 1.0E+15 ohms·cm |
| dielectric strength | | IEC 60243-1 | 30 KV/mm |
| relative permittivity | 100 Hz | IEC 60250 | 3.10 |
| relative permittivity | 1 MHz | IEC 60250 | 3.00 |
| Dissipation Factor | 100 Hz | IEC 60250 | 1.0E-3 |
| Dissipation Factor | 1 MHz | IEC 60250 | 9.0E-3 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 2 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 142 °C |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 129 °C |
| vicat | | ISO 306/B50 | 149 °C |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 7.0E-5 cm/cm/°C |
| Linear coefficient of thermal expansion | 横向 | ISO 11359-2 | 7.0E-5 cm/cm/°C |
| RTI Elec | 0.75 mm | UL 746 | 125 °C |
| RTI Imp | 0.75 mm | UL 746 | 115 °C |
| RTI | 0.75 mm | UL 746 | 125 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.