PA66 Isocor™ CU145SI SHAKESPEARE USA

مقایسه

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Charpy Notched Impact Strength	23℃	kJ/m²	0.556to4.643
Impact strength of simply supported beam without notch	23℃	kJ/m²	10.679to23.215
Impact strength of cantilever beam gap	23℃	kJ/m²	1.988to6.176

flammability	روش آزمون	نتیجه آزمون
Extreme Oxygen Index	%	21to28
Burning wire flammability index	°C	954to960
Hot filament ignition temperature	°C	743to960

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
crack			40.0to171.72 Mpa
crack	crack		%	3,0到77
yield			39.03to89.66 Mpa
crack			79.31to84.83 Mpa
crack	crack		%	2,2到12
Friction coefficient			0.30-1.0
Nominal tensile fracture strain	23℃	%	5,6到50
Tensile modulus	23℃		477.24到0.01,0.04E0.05 Mpa
yield		%	3,0到21
yield	yield			64.76to85.52 Mpa

thermal performance	روش آزمون	نتیجه آزمون
Continuous use temperature	°C	87to202
flow	mm/mm/°C	96.5E-5-152.4E-5
transverse	mm/mm/°C	99.1E-5-203.2E-5
Vicat softening temperature	°C	67to247
flow	mm/mm/°C	99.1E-5-101.6E-5

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
saturated		%	9.0
Apparent density		g/cm³	0.70-0.78
Stickiness		cm³/g	138to247
balance		%	2.5
melt mass-flow rate	235°C/1.0kg	g/10min	1.2-5.0
flow		mm/mm	152.4E-3-0.635
saturated		%	7,9到11
balance		%	2.5-3.5

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Surface resistivity		ohms	1.0E+2-2.5E+13
Dissipation factor	23℃		0.020-0.30
Volume resistivity	相对电容率(23℃)		3.50
Compared to the anti leakage trace index		V	PLC 0

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Ball Pressure Test			45.03to201.38 Mpa
Shore hardness	23℃		77to80

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.