impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	18	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	65	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
flammability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Flammability level		UL 94	HB
Burning wire flammability index	1.5 mm	IEC 60695-2-12	700	°C
Burning wire flammability index	Burning wire flammability index	2.0 mm	IEC 60695-2-12	700	°C
Hot filament ignition temperature	1.5 mm	IEC 60695-2-13	725	°C
Hot filament ignition temperature	Hot filament ignition temperature	2.0 mm	IEC 60695-2-13	725	°C
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Tensile modulus		ISO 527-2	2000	Mpa
tensile strength	Yield	ISO 527-2	50.0	Mpa
Tensile strain	Yield	ISO 527-2	4.0	%
Nominal tensile fracture strain		ISO 527-2	> 50	%
Bending modulus		ISO 178	1600	Mpa
bending strength		ISO 178	65.0	Mpa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	130	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	55.0	°C
Linear coefficient of thermal expansion	Flow	ISO 11359-2	1.2E-4	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	1.2E-4	cm/cm/°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
density		ISO 1183	1.07	g/cm³
Shrinkage rate	横向Flow	ISO 294-4	1.7	%
Shrinkage rate	Shrinkage rate	Flow	ISO 294-4	1.4	%
Water absorption rate	Saturation, 23°C	ISO 62	8.5	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	2.3	%
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Surface resistivity		IEC 60093	--	ohms
Volume resistivity		IEC 60093	1.0E+15	ohms·cm
Dielectric strength		IEC 60243-1	27	KV/mm
Relative permittivity	100 Hz	IEC 60250	3.10
Relative permittivity	Relative permittivity	1 MHz	IEC 60250	2.70
Dissipation factor	100 Hz	IEC 60250	3.0E-3
Dissipation factor	Dissipation factor	1 MHz	IEC 60250	0.016
Compared to the anti leakage trace index		IEC 60112		V