PBT POCAN® BF 4212 000000 LANXESS GERMANY

ویژگی‌ها:

Filler glass fiber reinforced material 15% filler by weight

توصیف محصول

گواهی‌نامه‌ها(0)

جدول خواص

توصیف محصول

ویژگی‌ها:

Filler | glass fiber reinforced material | 15% | filler by weight

گواهی‌نامه‌ها

No Data...

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	<10	kJ/m²
	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	<10	kJ/m²
	Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	<10	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	40	kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	<10	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	<10	kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	30	kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	<10	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	40	kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	<10	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	<10	kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	30	kJ/m²
flammability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
UL flame retardant rating	0.75mm	UL 94	V-0
	UL flame retardant rating	1.5mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	V-0
Burning wire flammability index	0.75mm	IEC 60695-2-12	960	°C
	Burning wire flammability index	1.5mm	IEC 60695-2-12	960	°C
	Burning wire flammability index	Burning wire flammability index	3.0mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	0.75mm	IEC 60695-2-13	850	°C
	Hot filament ignition temperature	1.5mm	IEC 60695-2-13	750	°C
	Hot filament ignition temperature	Hot filament ignition temperature	3.0mm	IEC 60695-2-13	725	°C
Extreme Oxygen Index		ISO 4589-2	28	%
Burning wire flammability index	0.75mm	IEC 60695-2-12	960	°C
	Burning wire flammability index	1.5mm	IEC 60695-2-12	960	°C
	Burning wire flammability index	Burning wire flammability index	3.0mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	0.75mm	IEC 60695-2-13	850	°C
Hot filament ignition temperature	Hot filament ignition temperature	1.5mm	IEC 60695-2-13	750	°C
UL flame retardant rating	0.75mm	UL 94	V-0
	UL flame retardant rating	1.5mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	V-0
Hot filament ignition temperature	3.0mm	IEC 60695-2-13	725	°C
Extreme Oxygen Index		ISO 4589-2	28	%
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Tensile modulus	23°C	ISO 527-2/1	7000	MPa
tensile strength	Break,23°C	ISO 527-2/5	110	MPa
Tensile strain	Break,23°C	ISO 527-2/5	2.6	%
Bending modulus	23°C	ISO 178/A	6500	MPa
bending strength	23°C	ISO 178/A	170	MPa
Bending strain	23°C	ISO 178/A	3.5	%
Tensile strain	Break,23°C	ISO 527-2/5	2.6	%
Bending modulus	23°C	ISO 178/A	6500	MPa
bending strength	23°C	ISO 178/A	170	MPa
Bending strain	23°C	ISO 178/A	3.5	%
Tensile modulus	23°C	ISO 527-2/1	7000	MPa
tensile strength	Break,23°C	ISO 527-2/5	110	MPa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Ball Pressure Test	212°C	IEC 60695-10-2	通过
Melting temperature		ISO 11357-3	222	°C
Linear coefficient of thermal expansion	MD:23to55°C	ISO 11359-2	4E-05	cm/cm/°C
	Linear coefficient of thermal expansion	TD:23to55°C	ISO 11359-2	1.1E-04	cm/cm/°C
		Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	4E-05	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	1.1E-04	cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	215	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	190	°C
Vicat softening temperature		ISO 306/B50	212	°C
Ball Pressure Test	212°C	IEC 60695-10-2	Pass
Melting temperature		ISO 11357-3	222	°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	215	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	190	°C
Vicat softening temperature		ISO 306/B50	212	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.20	%
density	23°C	ISO 1183	1.53	g/cm³
Melt Volume Flow Rate (MVR)	260°C/2.16kg	ISO 1133	14.0	cm³/10min
Shrinkage rate	TD:260°C,2.00mm2	ISO 2577	1.1	%
	Shrinkage rate	TD:120°C,4hr,2.00mm3	ISO 2577	0.10	%
		Shrinkage rate	MD:260°C,2.00mm2	ISO 2577	0.70	%
		Shrinkage rate	Shrinkage rate	MD:120°C,4hr,2.00mm3	ISO 2577	0.10	%
Water absorption rate	Saturation,23°C	ISO 62	0.40	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.20	%
density	23°C	ISO 1183	1.53	g/cm³
Melt Volume Flow Rate (MVR)	260°C/2.16kg	ISO 1133	14.0	cm³/10min
Shrinkage rate	TD:260°C,2.00mm2	ISO 2577	1.1	%
	Shrinkage rate	TD:120°C,4hr,2.00mm3	ISO 2577	0.10	%
		Shrinkage rate	MD:260°C,2.00mm2	ISO 2577	0.70	%
		Shrinkage rate	Shrinkage rate	MD:120°C,4hr,2.00mm3	ISO 2577	0.10	%
Water absorption rate	Saturation,23°C	ISO 62	0.40	%
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Surface resistivity		IEC 60093	>1.0E+17	ohms
Volume resistivity	23°C	IEC 60093	>1.0E+16	ohms·cm
Dielectric strength	23°C,1.00mm	IEC 60243-1	29	kV/mm
Compared to the anti leakage trace index	CTI	UL 746	PLC 3
Compared to the anti leakage trace index	Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 3
Surface resistivity		IEC 60093	>1.0E+17	ohms
Volume resistivity	23°C	IEC 60093	>1.0E+16	ohms·cm
Dielectric strength	23°C,1.00mm	IEC 60243-1	29	kV/mm
Compared to the anti leakage trace index	CTI	UL 746	PLC 3
Compared to the anti leakage trace index	Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 3
Supplementary Information	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
ISO Shortcut		ISO 7792	PBT.GFHMR.09-070.GF15
ISO Shortcut	ISO Shortcut		ISO 7792	PBT.GFHMR.09-070.GF15