PA66 A 30 S FN31 000000 LANXESS GERMANY

توصیف محصول

گواهی‌نامه‌ها(0)

جدول خواص

توصیف محصول

گواهی‌نامه‌ها

No Data...

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Charpy Notched Impact Strength	23°C	ISO 179/1eA	<10	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	50	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	60	kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	<10	kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	55	kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	55	kJ/m²
flammability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Extreme Oxygen Index		ISO 4589-2	34	%
Burning wire flammability index	0.40mm	IEC 60695-2-12	960	°C
Ignition temperature of heating wire	0.40mm	IEC 60695-2-13	775	°C
UL flame retardant rating	0.40mm	UL 94	V-0
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
bending strength	FlexuralStrainatFlexuralStrength5(23°C)		5.8	%
Tensile modulus	23°C	ISO 527-2/1	3800	MPa
tensile strength	Yield,23°C	ISO 527-2/50	85.0	MPa
Tensile strain	Yield,23°C	ISO 527-2/50	4.1	%
Bending modulus	23°C	ISO 178/A	3700	MPa
bending strength	3.5%Strain	ISO 178/A	120	MPa
bending strength	bending strength	23°C	ISO 178	125	MPa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	212	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	80.0	°C
Vicat softening temperature		ISO 306/B120	230	°C
Melting temperature		ISO 11357-3	265	°C
Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	8E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	7E-05	cm/cm/°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
density	23°C	ISO 1183	1.17	g/cm³
Shrinkage rate	TD:270°C,2.00mm2	ISO 294-4	1.1	%
	Shrinkage rate	TD:120°C,2hr,2.00mm3	ISO 294-4	0.10	%
		Shrinkage rate	MD:270°C,2.00mm2	ISO 294-4	1.1	%
		Shrinkage rate	Shrinkage rate	MD:120°C,2hr,2.00mm3	ISO 294-4	0.10	%
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Surface resistivity		IEC 60093	1E+15	ohms
Volume resistivity	23°C	IEC 60093	1E+14	ohms·cm
Dielectric strength	23°C,1.00mm	IEC 60243-1	30	kV/mm
Relative permittivity	23°C,100Hz	IEC 60250	4.00
Relative permittivity	Relative permittivity	23°C,1MHz	IEC 60250	4.00
Dissipation factor	23°C,100Hz	IEC 60250	0.012
Dissipation factor	Dissipation factor	23°C,1MHz	IEC 60250	0.019
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 0
Supplementary Information	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
ISO Shortcut		ISO 1874	PA66.GFHR.12-040;ISO1043PAFR(30)

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.