برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ISO 1183 | 1.35 g/cm³ |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 6.5 % |
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 1.5 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 0.8mm | UL 94 | V-0 |
| Burning wire flammability index | 1.0mm | IEC 60695-2-12 | 960 °C |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 1.0mm | IEC 60695-2-13 | >775 °C |
| Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | >775 °C |
| burning rate | | FMVSS302 | 0.0 mm/min |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | | ISO 527-2/1A/1 | 3100 MPa |
| tensile strength | Yield | ISO 527-2/1A/50 | 55.0 MPa |
| Nominal tensile fracture strain | | ISO 527-2/1A/50 | 20 % |
| Flexural modulus | | ISO 178 | 3000 MPa |
| bending strength | | ISO 178 | 80.0 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 5.0 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 2 |
| Surface Resistivity | | IEC 60093 | 1E+12 ohms |
| Volume resistivity | | IEC 60093 | 1E+15 ohms·cm |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/Af | 85.0 °C |
| vicat | | ISO 306/B50 | 205 °C |
| melting temperature | | ISO 11357 | 260 °C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/Bf | 180 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.