برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ISO 11832 | 1200 kg/m³ |
| melt mass-flow rate | 300°C/1.2kg | ISO 1133 | 10 g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO 11332 | 8.00 cm³/10min |
| Shrinkage rate | MD | ISO 294-4 | 0.50to0.70 % |
| density | | ISO 1183/A | 1.20 g/cm³ |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| transmissivity | | ASTM D1003 | 87.0to91.0 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| Burning Behav. | 1.60mm,UL | ISO 12102 | HB |
| Burning Behav.atthicknessh | 3.20mm,UL | ISO 12102 | HB |
| Limiting Oxygen Index (LOI) | | ISO 4589-22 | 26 % |
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | | ISO 527-2/50 | 2300 MPa |
| Tensile modulus | | ISO 527-22 | 2300 MPa |
| tensile strength | Yield | ISO 527-2/50 | 60.0 MPa |
| tensile strength | Yield | ISO 527-22 | 60.0 MPa |
| tensile strength | Break | ISO 527-2/50 | 71.0 MPa |
| Tensile strain | Yield | ISO 527-2/50 | 6.0 % |
| Tensile strain | Yield | ISO 527-22 | 6.0 % |
| Tensile strain | Break | ISO 527-2/50 | 150 % |
| Nominal fracture strain | | ISO 527-22 | >50 % |
| Flexural modulus | | ISO 178 | 2400 MPa |
| bending strength | | ISO 178 | 97.0 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA2 | 90.0 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA2 | 13.0 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eU2 | NoBreak |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eU2 | NoBreak |
| Impact strength of cantilever beam gap | 23°C | ISO 180/4A | 88 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180 | NoBreak |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Volume resistivity | | IEC 600932 | >1.0E+13 ohms·m |
| dielectric strength | | IEC 60243-12 | 17 kV/mm |
| relative permittivity | 100Hz | IEC 602502 | 3.00 |
| relative permittivity | 1MHz | IEC 602502 | 3.00 |
| Dissipation Factor | 100Hz | IEC 602502 | 1E-03 |
| Dissipation Factor | 1MHz | IEC 602502 | 2E-03 |
| Compared to the Leakage Tracking Index (CTI) | 2.00mm | IEC 60112 | PLC 2 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Linear coefficient of thermal expansion | MD | ISO 11359-22 | 7E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,退火，HDT | ISO 75-2/B | 144 °C |
| Heat distortion temperature | 0.45MPa，HDT | ISO 75-22 | 145 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 125 °C |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 141 °C |
| Heat distortion temperature | 1.8MPa，HDT | ISO 75-22 | 131 °C |
| vicat | | ISO 306/B50 | 149 °C |
| vicat | 50N | ISO 3062 | 149 °C |
| Ball pressure temperature | | IEC 60335-1 | 125 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.